| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.69 g/cm³
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
0.54 % | ASTM D 955 | 24 hrs |
横向(Across Flow) |
0.57 % | ASTM D 955 | 24 hrs |
吸水率 | 0.06 %
| ISO 62-1 | 23°C/24hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
78 Mpa | ISO 527 | 5 mm/min |
断裂(brk) |
77 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
0.7 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) |
0.8 % | ISO 527 | 5 mm/min |
弯曲强度 | | | |
断裂(brk) |
127 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
断裂(brk) |
128 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 11000 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 12000 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 13700 Mpa
| ASTM D638 | 5 mm/min |
拉伸模量 | 13000 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
21 J/m | ASTM D256 | |
23℃ (73℉) |
3 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
235 J/m | ASTM D4812 | |
23℃ (73℉) |
16 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
205 °C | ASTM D648 | 3.2 mm |
0.45 Mpa (66 psi)（4.6kg/cm²） |
204 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
174 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
162 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
30.8 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) |
23.5 E-6/°C | ASTM E831 | 40°C to 120°C, flow |
横向(Across Flow) |
47.7 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) |
52.5 E-6/°C | ASTM E831 | 40°C to 120°C, xflow |
导热系数 | 3.4 W/(m K)
| ASTM E 1461 | in-plane, ?25*0.4mm disc |
导热系数 | 2 W/(m K)
| ASTM E 1461 | through-plane, 10*10*3mm sample |
导热系数 | 3.3 W/(m K)
| ISO 22007 | in-plane, 60*60*3mm plaque |
导热系数 | 1 W/(m K)
| ISO 22007 | through-plane, 60*60*3mm plaque |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
V-0 |
0.8 mm | UL94 | |
灼热丝可燃性指数(GWFI) | | | |
1mm |
960 °C | IEC 60695-2-12 | passes at |
1.5mm |
960 °C | IEC 60695-2-12 | passes at |
3mm |
960 °C | IEC 60695-2-12 | passes at |
灼热丝点燃温度(GWIT) | | | |
1.0mm |
800 °C | IEC 60695-2-13 | |
3.0mm |
850 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1.0E+15 Ohm
| ASTM D257 | |
介电常数(DK) | | | |
1.1 GHz |
4.86 - | ASTM ES 7-83 | |
耗散因数(DF) | | | |
1.1 GHz |
103 E-4 | ASTM ES 7-83 | |
相比漏电起痕指数(CTI ) | | | |
- |
600 V | IEC 60112 | |
绝缘强度 | 10 kV/mm
| ASTM D149 | in oil, 1.0 mm |
热线圈起燃性(HWI) | 1 PLC
| UL 746A | |
高电流弧起燃性(HAI) | 0 PLC
| UL 746A | surface |