ICORENE® XE00011 is an experimental polyamide 6 based natural powder (PA6) containing stabiliser additives specifically designed for rotomoulding.
This grade is used for making rotomoulded parts typically used in high heat applications or for long term hot water contact.
The parts made using this material require post moulding conditioning in moist air or in water to achieve full impact resistance and ductility.
This powder may be rotational moulded without using an inert gas (N2 or CO2) atmosphere.
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.14 g/cm³
| ASTM D 1505 | Black |
吸水率 | 3 %
| ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
53 Mpa | ISO 527-2/1A/50 | Cond., 3.20 mm, Rotational Molded |
屈服(yld) |
78 Mpa | ISO 527-2/1A/50 | Dry, 3.20 mm, Rotational Molded |
拉伸延伸率 | | | |
屈服(yld) |
25 % | ISO 527-2/1A/50 | Cond., 3.20 mm, Rotational Molded |
屈服(yld) |
4 % | ISO 527-2/1A/50 | Dry, 3.20 mm, Rotational Molded |
断裂(brk) |
80 % | ISO 727-2/1A/50 | Cond., 3.20 mm, Rotational Molded |
断裂(brk) |
25 % | ISO 727-2/1A/50 | Dry, 3.20 mm, Rotational Molded |
弯曲模量 | 1700 Mpa
| ASTM D790 | Cond., 3.20 mm, Rotational Molded |
弯曲模量 | 2800 Mpa
| ASTM D790 | Dry, 3.20 mm, Rotational Molded |
拉伸模量 | 1500 Mpa
| ISO 527-1/1A/50 | Cond., 3.20 mm, Rotational Molded |
拉伸模量 | 3200 Mpa
| ISO 527-1/1A/50 | Dry, 3.20 mm, Rotational Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
23℃ (73℉) |
4.8 kJ/m² | ISO 179/1eA | DRY, injection moulded |
落锤冲击 | 49 J
| ARM | 23°C, 3.20 mm, Rotational Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
185 °C | ISO 75-2/B | Annealed, 3.20 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
55 °C | ISO 75/Ae | Unannealed, 3.20 mm |
维卡软化温度(Vicat) | 195 °C
| ISO 306/B50 | |
熔融温度(Tm) | 221 °C
| DSC | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
V-2 |
1.5 mm | UL94 | |
FMVSS | 0 mm/min
| FMVSS 302 | 2.00 mm |
燃烧速率 | 0 mm/min
| ISO 3795 | 2.00 mm |