KOPLA® KNG1050
PA6
科普拉(KOPLA)
产品描述
* Desciription PA6 Glass fiber 50% reinforced * Caracteristics Rigidity, High modulus, High strength * Application Automobile : Underhood parts, Interior/Exterior parts etc Electric/Electronics : Bobbin, Connector, Electronic tools etc Other industries : Chair base, Inline skate, Joint etc
基本信息
| 原厂资料 | 物性表-ASTM(中英文) | |||
| 产品特性 | 高强度高刚性填充增强 | |||
| 增强填充 | 50% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.56 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.1~0.5 % | ASTM D 955 | 3T |
横向(Across Flow) | 0.3~0.7 % | ASTM D 955 | 3T |
吸水率 | 0.75 % | ASTM D570 | 23°C, Water 24h |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 225 Mpa | ASTM D 638 | 23°C |
- | 150 Mpa | ASTM D 638 | RH50 |
拉伸延伸率 | |||
- | 2 % | ASTM D 638 | 23°C |
- | 3 % | ASTM D 638 | RH50 |
弯曲强度 | |||
- | 360 Mpa | ASTM D790 | 23°C |
- | 270 Mpa | ASTM D790 | RH50 |
弯曲模量 | 14500 Mpa | ASTM D790 | 23°C |
弯曲模量 | 8500 Mpa | ASTM D790 | RH50 |
拉伸模量 | 14600 Mpa | ASTM D638 | 23°C |
拉伸模量 | 8600 Mpa | ASTM D638 | RH50 |
泊松比 | 0.35 - | ASTM D 638 | 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 17 kJ/m² | ASTM D256 | |
23℃ (73℉) | 29 kJ/m² | ASTM D256 | RH50 |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 125 R | ASTM D785 | |
洛氏硬度R | 115 R | ASTM D785 | RH50 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 220 °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 215 °C | ASTM D648 | |
线性膨胀系数(CLTE) | |||
- | 18 E-6/K | ASTM D 696 | |
熔融温度(Tm) | 222 °C | Internal | DSC |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | ASTM D257 | |
介电常数(DK) | |||
1MHz | 3.8 - | ASTM D 150 | |
耗散因数(DF) | |||
1MHz | 200 E-4 | ASTM D150 | |
绝缘强度 | 22 kV/mm | ASTM D149 |