AKROMID® B3 GF 50 2 S1 black (3050)
AKROMID® B3 GF 50 2 S1 black (3050)
PA6
安科罗/开德阜(AKRO-PLASTIC)
产品描述
AKROMID® B3 GF 50 2 S1 black (3050) is a
50% glass fiber reinforced, impact modified
Polyamide 6. It is characterised by very high
stiffness and strength as well as a higher
notched impact strength compared to a
standard PA 6 GF 50. Furthermore, it is UV
stabilised. The material is therefore
perfectly suitable for industrial applications
and for housings and covers in the
automotive industry.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 高强度高刚性增韧/冲击改性抗紫外线填充增强 |
| 添加助剂 | 紫外线稳定剂抗冲击剂 |
| 颜色形状 | 粒状黑色 |
| 成型方式 | 注塑 |
| 增强填充 | 50% 玻纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.54 g/cm³
| ISO 1183 | 23°C |
收缩率 | | | |
纵向(Flow) |
0.1~0.3 % | ISO 294-4 | |
横向(Across Flow) |
0.4~0.6 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
120 Mpa | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) |
195 Mpa | ISO 527-2 | Dry, 5 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
8 % | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) |
4 % | ISO 527-2 | Dry, 5 mm/min |
拉伸模量 | 7800 Mpa
| ISO 527-2 | Cond., 1 mm/min |
拉伸模量 | 15000 Mpa
| ISO 527-2 | Dry, 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
20 kJ/m² | ISO 179-1/1eA | Cond. |
-30℃ (-22℉) |
20 kJ/m² | ISO 179-1/1eA | Dry |
23℃ (73℉) |
40 kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) |
27 kJ/m² | ISO 179-1/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
105 kJ/m² | ISO 179-1/1eU | Dry |
23℃ (73℉) |
NB kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) |
110 kJ/m² | ISO 179-1/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
210 °C | ISO 75/A | |
熔融温度(Tm) | 220 °C
| ISO 11357-3 | DSC, 10K/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
1.6 mm | UL94 | |
FMVSS | + pass
| FMVSS 302 | > 1 mm Thickness |