Ultramid® B3U50G6
PA6
巴斯夫 (BASF)
产品描述
Without halogens flame retardant glass fiber reinforced injection moulding grade for plastic parts in electrical applications. The product is light colorable and provides good mechanical and electrical properties. Due to the halide free stabilization the impact on corrosion is minimized and sensitive electronic components are better protected. In particular optimized for the glow wire requirements of IEC 60335.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无卤填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.5 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
275°C/5 kg | 25 cm³/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.25 % | ISO 294-4 | |
横向(Across Flow) | 0.8 % | ISO 294-4 | |
吸水率 | 5.5~5.7 % | ISO 62 | saturation in water at 23°C |
吸湿率 | 1.5~1.7 % | ISO 62 | equilibrium 23°C/50% r.h. |
粘度 | 115 cm³/g | ISO 307, 1157, 1628 | 0.5% in 96% H2SO4 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 115 Mpa | ISO 527-1/-2 | Cond. |
断裂(brk) | 170 Mpa | ISO 527-1/-2 | Dry |
拉伸延伸率 | |||
断裂(brk) | 3.9 % | ISO 527-1/-2 | Cond. |
断裂(brk) | 2.9 % | ISO 527-1/-2 | Dry |
弯曲强度 | |||
- | 180 Mpa | ISO 178 | Cond. |
- | 250 Mpa | ISO 178 | Dry |
弯曲模量 | 8000 Mpa | ISO 178 | Cond. |
弯曲模量 | 11500 Mpa | ISO 178 | Dry |
拉伸模量 | 8200 Mpa | ISO 527-1/-2 | Cond. |
拉伸模量 | 11500 Mpa | ISO 527-1/-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 8.5 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | 7 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 45 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 70 kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | 65 kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 220 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 210 °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 23 E-6/K | ISO 11359-1/-2 | (23-55)°C |
横向(Across Flow) | 82 E-6/K | ISO 11359-1/-2 | (23-55)°C |
熔融温度(Tm) | 220 °C | ISO 11357-1/-3 | DSC |
加工温度 | 240~265 °C | - | Injection moulding/Extrusion |
模具温度 | 80~90 °C | - | Injection moulding |
温度指数(TI)-拉伸强度 | |||
5000 h | 180 °C | IEC 60216 | 50% loss of tensile strength |
20000 h | 165 °C | IEC 60216 | 50% loss of tensile strength |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.75 mm | UL94 | |
5VA | 1.5 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
0.75mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.75mm | 775 °C | IEC 60695-2-13 | |
欧洲轨道车辆认证 | 2 HL | EN 45545-2 | 0,8 - 3mm |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+8 Ohm-m | IEC 62631-3-1 | Cond. |
体积电阻率 | 1.0E+12 Ohm-m | IEC 62631-3-1 | Dry |
表面电阻率 | 1.0E+12 Ohm | IEC 62631-3-2 | Cond. |
介电常数(DK) | |||
1MHz | 4.7 - | IEC 62631-2-1 | Cond. |
1MHz | 4.1 - | IEC 62631-2-1 | Dry |
耗散因数(DF) | |||
1MHz | 730 E-4 | IEC 62631-2-1 | Cond. |
1MHz | 170 E-4 | IEC 62631-2-1 | Dry |
相比漏电起痕指数(CTI ) | |||
溶液A | 450 V | IEC 60112 | |
绝缘强度 | 39 kV/mm | IEC 60243-1 | Dry, K20/K20, (60*60*1 mm³) |