Durethan® BC550Z 900116 DUSXBL
PA6
朗盛 (LANXESS)
产品描述
PA 6, non-reinforced, blow molding, improved impact strength, heat-aging stabilized. For the use in tank systems and pressure vessels
ISO Shortname: ISO 16396-PA 6-I,,BHR,S14-020
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高冲击耐热老化 | |||
| 成型方式 | 吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.07 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.2 % | ISO 294-4 | 60x60x2; 120℃; 4 h |
纵向(Flow) | 1.5 % | ISO 294-4 | 60x60x2; 260℃/MT80℃;600 bar |
横向(Across Flow) | 0.2 % | ISO 294-4 | 60x60x2; 120℃; 4 h |
横向(Across Flow) | 1.5 % | ISO 294-4 | 60x60x2; 260℃/MT80℃;600 bar |
吸水率 | 2.5 % | ISO 62 | Equilibrium, 23°C, 50% RH |
吸水率 | 9.1 % | ISO 62 | Saturation, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 4 Mpa | ISO 527-1/-2 | Dry,50mm/min |
屈服(yld) | 50 Mpa | ISO 527-1/-2 | Dry,50mm/min |
拉伸延伸率 | |||
标称断裂伸长率 | 140 % | ISO 527-1/-2 | Dry,50mm/min |
标称断裂伸长率 | 165 % | ISO 527-1/-2 | cond. ,50mm/min |
弯曲强度 | |||
3.5%应变 | 55 Mpa | ISO 178/A | Dry,2mm/min |
3.5%应变 | 14 Mpa | ISO 178/A | cond. ,2mm/min |
- | 66 Mpa | ISO 178/A | Dry,2mm/min |
- | 21 Mpa | ISO 178/A | cond. ,2mm/min |
弯曲应变 | |||
- | 6 % | ISO 178/A | Dry,2mm/min |
- | 9 % | ISO 178/A | cond. ,2mm/min |
弯曲模量 | 1800 Mpa | ISO 178/A | Dry,2mm/min |
弯曲模量 | 470 Mpa | ISO 178/A | cond. ,2mm/min |
拉伸模量 | 2000 Mpa | ISO 527-1/-2 | Dry,1mm/min |
拉伸模量 | 430 Mpa | ISO 527-1/-2 | cond. ,1mm/min |
冲孔性能 | |||
力 | 5700 N | ISO 6603-2 | Dry,-30℃ |
力 | 5000 N | ISO 6603-2 | Dry,23℃ |
能量 | 67 J | ISO 6603-2 | Dry,-30℃ |
能量 | 65 J | ISO 6603-2 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 25 kJ/m² | ISO 179/1eA | Dry |
-30℃ (-22℉) | 25 kJ/m² | ISO 179/1eA | cond. |
23℃ (73℉) | 100 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 130 kJ/m² | ISO 179/1eA | cond. |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Dry |
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | cond. |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | cond. |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 25 kJ/m² | ISO 180/1A | Dry |
-30℃ (-22℉) | 25 kJ/m² | ISO 180/1A | cond. |
23℃ (73℉) | 85 kJ/m² | ISO 180/1A | Dry |
23℃ (73℉) | 105 kJ/m² | ISO 180/1A | cond. |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | Dry |
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | cond. |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | Dry |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | cond. |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 53 °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 140 E-6/K | ISO 11359-1/-2 | 23 to 55℃ |
横向(Across Flow) | 130 E-6/K | ISO 11359-1/-2 | 23 to 55℃ |
熔融温度(Tm) | 219 °C | ISO 11357-1/-3 | 10℃/min |
加工温度 | 260 °C | - | Injection molding |
模具温度 | 80 °C | - | Injection molding |