Ultramid® B3ZG6
PA6
巴斯夫 (BASF)
产品描述
Ultramid B3ZG6 is an impact-modified, 30% glass fiber reinforced injection molding PA6 grade for industrial items having very high impact strength and rigidity.
Applications
Typical applications include automotive airbag housings and half-shells for suitcases.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 高刚性高冲击填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.33 g/cm³ | ISO 1183 | |
比重 | 1.33 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
275°C/5 kg | 25 cm³/10 min | ISO 1133 | |
收缩率 | |||
- | 0.3 % | Internal | 1/8" bar |
吸水率 | 2 % | ASTM D570 | 50% RH |
吸水率 | 6.2 % | ASTM D570 | Saturation |
吸水率 | 2 % | ISO 62 | 50% RH |
吸水率 | 6.2 % | ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 100 Mpa | ISO 527 | Conditioned,23℃ |
断裂(brk) | 150 Mpa | ISO 527 | Dry,23℃ |
断裂(brk) | 138 Mpa | ASTM D638 | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 3.6 % | ASTM D638 | Dry,23℃ |
断裂(brk) | 10 % | ISO 527 | Conditioned,23℃ |
断裂(brk) | 3.6 % | ISO 527 | Dry,23℃ |
弯曲强度 | |||
- | 220 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 7860 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 4700 Mpa | ISO 178 | Conditioned,23℃ |
弯曲模量 | 7400 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 5300 Mpa | ISO 527 | Conditioned,23℃ |
拉伸模量 | 9000 Mpa | ISO 527 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 15 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 35 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 20 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 90 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 110 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 95 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 139 J/m | ASTM D256 | Dry |
-30℃ (-22℉) | 10 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | 192 J/m | ASTM D256 | Dry |
23℃ (73℉) | 32 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | 20 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 220 °C | ASTM D648 | Dry |
0.45 Mpa (66 psi)（4.6kg/cm²） | 220 °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 207 °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 200 °C | ISO 75 | Dry |
相对温度指数(RTI) | |||
冲击w/impact,0.73mm | 115 °C | UL 746B | |
冲击w/impact,1.5/1.6 mm | 115 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm | 120 °C | UL 746B | |
电气Elec,0.73mm | 150 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 150 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 150 °C | UL 746B | |
强度w/o impact,0.73mm | 150 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm | 150 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm | 150 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 23 E-6/°C | Internal | Dry |
横向(Across Flow) | 65 E-6/°C | Internal | Dry |
- | 10 E-6/°C | ASTM D E831 | Dry |
熔融温度(Tm) | 220 °C | ASTM D3418 | Dry |
熔融温度(Tm) | 220 °C | ISO 3146 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.73 mm | UL94 | |
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+10 Ohm-m | ASTM D257 | Conditioned,1.50 mm |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | Dry,1.50 mm |
体积电阻率 | 1.0E+10 Ohm-m | IEC 60093 | Conditioned |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | Dry |
介电常数(DK) | |||
1MHz | 6.8 - | IEC 60250 | Conditioned |
1MHz | 3.8 - | IEC 60250 | Dry |
耗散因数(DF) | |||
1MHz | 2000 E-4 | IEC 60250 | Conditioned |
1MHz | 200 E-4 | IEC 60250 | Dry |