Ultramid® 8202 HS
PA6
巴斯夫 (BASF)
产品描述
Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose PA6 injection molding. It possesses the combination of strength and toughness and has excellent chemical and abrasion resistance. The heat stabilizer system extends the retention of properties at the more elevated temperatures. Excellent in filling thin walls or areas.
Applications
Ultramid 8202 HS is generally recommended for drapery hardware, gears, fittings, furniture casters, bearings, handles, clips, fasteners and thin parts.
基本信息
| 原厂资料 | 物性表-ASTM(英文) 物性表-ISO(英文) | |||
| 产品特性 | 热稳定耐磨耐化学性低粘度 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.13 g/cm³ | ISO 1183 | |
比重 | 1.13 - | ASTM D792 | |
收缩率 | |||
- | 1.2 % | Internal | |
吸水率 | 1.6 % | ASTM D570 | 24 hr |
吸水率 | 2.7 % | ASTM D570 | 50% RH |
吸水率 | 9.5 % | ASTM D570 | Saturation |
吸水率 | 1.6 % | ISO 62 | 24 hr |
吸水率 | 2.7 % | ISO 62 | 50% RH |
吸水率 | 9.5 % | ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 110 Mpa | ASTM D638 | Conditioned,-40℃ |
屈服(yld) | 20 Mpa | ASTM D638 | Conditioned,121℃ |
屈服(yld) | 36 Mpa | ASTM D638 | Conditioned,23℃ |
屈服(yld) | 30 Mpa | ASTM D638 | Conditioned,80℃ |
屈服(yld) | 126 Mpa | ASTM D638 | Dry,-40℃ |
屈服(yld) | 25 Mpa | ASTM D638 | Dry,121℃ |
屈服(yld) | 79 Mpa | ASTM D638 | Dry,23℃ |
屈服(yld) | 35 Mpa | ASTM D638 | Dry,80℃ |
屈服(yld) | 110 Mpa | ISO 527 | Conditioned,-40℃ |
屈服(yld) | 20 Mpa | ISO 527 | Conditioned,120℃ |
屈服(yld) | 15 Mpa | ISO 527 | Conditioned,150℃ |
屈服(yld) | 36 Mpa | ISO 527 | Conditioned,23℃ |
屈服(yld) | 30 Mpa | ISO 527 | Conditioned,80℃ |
屈服(yld) | 126 Mpa | ISO 527 | Dry,-40℃ |
屈服(yld) | 25 Mpa | ISO 527 | Dry,120℃ |
屈服(yld) | 20 Mpa | ISO 527 | Dry,150℃ |
屈服(yld) | 78 Mpa | ISO 527 | Dry,23℃ |
屈服(yld) | 35 Mpa | ISO 527 | Dry,80℃ |
断裂(brk) | 60 Mpa | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 75 Mpa | ASTM D638 | Dry,23℃ |
拉伸延伸率 | |||
屈服(yld) | 40 % | ASTM D638 | Conditioned,121℃ |
屈服(yld) | 16 % | ASTM D638 | Conditioned,23℃ |
屈服(yld) | 35 % | ASTM D638 | Conditioned,80℃ |
屈服(yld) | 36 % | ASTM D638 | Dry,121℃ |
屈服(yld) | 4 % | ASTM D638 | Dry,23℃ |
屈服(yld) | 4.2 % | ASTM D638 | Dry,80℃ |
屈服(yld) | 16 % | ISO 527 | Conditioned,23℃ |
屈服(yld) | 4 % | ISO 527 | Dry,23℃ |
断裂(brk) | 100 % | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 55 % | ASTM D638 | Dry,23℃ |
标称断裂伸长率 | 50 % | ISO 527 | Conditioned,23℃ |
标称断裂伸长率 | 25 % | ISO 527 | Dry,23℃ |
弯曲强度 | |||
- | 154 Mpa | ASTM D790 | Conditioned,-40℃ |
- | 35 Mpa | ASTM D790 | Conditioned,23℃ |
- | 170 Mpa | ASTM D790 | Dry,-40℃ |
- | 17 Mpa | ASTM D790 | Dry,121℃ |
- | 108 Mpa | ASTM D790 | Dry,23℃ |
- | 30 Mpa | ASTM D790 | Dry,65℃ |
- | 20 Mpa | ASTM D790 | Dry,90℃ |
- | 25 Mpa | ISO 178 | Conditioned,23℃ |
- | 85 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 3660 Mpa | ASTM D790 | Conditioned,-40℃ |
弯曲模量 | 740 Mpa | ASTM D790 | Conditioned,23℃ |
弯曲模量 | 3010 Mpa | ASTM D790 | Dry,-40℃ |
弯曲模量 | 305 Mpa | ASTM D790 | Dry,121℃ |
弯曲模量 | 2830 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 500 Mpa | ASTM D790 | Dry,65℃ |
弯曲模量 | 350 Mpa | ASTM D790 | Dry,90℃ |
弯曲模量 | 770 Mpa | ISO 178 | Conditioned,23℃ |
弯曲模量 | 2400 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 320 Mpa | ISO 527 | Conditioned,120℃ |
拉伸模量 | 310 Mpa | ISO 527 | Conditioned,150℃ |
拉伸模量 | 970 Mpa | ISO 527 | Conditioned,23℃ |
拉伸模量 | 550 Mpa | ISO 527 | Conditioned,80℃ |
拉伸模量 | 360 Mpa | ISO 527 | Dry,120℃ |
拉伸模量 | 290 Mpa | ISO 527 | Dry,150℃ |
拉伸模量 | 2700 Mpa | ISO 527 | Dry,23℃ |
拉伸模量 | 485 Mpa | ISO 527 | Dry,80℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 3.5 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 5.1 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | NB kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 83 J/m | ASTM D256 | Conditioned |
-40℃ (-40℉) | 48 J/m | ASTM D256 | Dry |
23℃ (73℉) | NB J/m | ASTM D256 | Conditioned |
23℃ (73℉) | 58 J/m | ASTM D256 | Dry |
落锤冲击 | 271 J | Internal | Conditioned,23℃ |
落锤冲击 | 142 J | Internal | Dry |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 119 R | ASTM D785 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 178 °C | ASTM D648 | Dry |
0.45 Mpa (66 psi)（4.6kg/cm²） | 150 °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 65 °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 60 °C | ISO 75 | Dry |
相对温度指数(RTI) | |||
冲击w/impact,0.71mm | 95 °C | UL 746B | |
冲击w/impact,1.5/1.6 mm | 105 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm | 105 °C | UL 746B | |
冲击w/impact,6.0mm | 105 °C | UL 746B | |
电气Elec,0.71mm | 130 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 130 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 130 °C | UL 746B | |
电气Elec,6.0mm | 130 °C | UL 746B | |
强度w/o impact,0.71mm | 95 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm | 105 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm | 105 °C | UL 746B | |
强度w/o impact,6.0mm | 105 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
- | 83 E-6 mm/mm/℃ | ASTM D E831 | Dry |
熔融温度(Tm) | 220 °C | ASTM D3418 | Dry |
熔融温度(Tm) | 220 °C | ISO 3146 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.71 mm | UL94 | |
V-2 | 1.5 mm | UL94 | |
V-2 | 3 mm | UL94 | |
V-2 | 6 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | Dry,1.50 mm |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | Dry |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | Dry |
绝缘强度 | 22 kV/mm | ASTM D149 | Dry,1.50 mm,Short-Time |
绝缘强度 | 37 kV/mm | IEC 60243-1 | Dry |