Ultramid® B3WG13 BK00102
PA6
巴斯夫 (BASF)
产品描述
Ultramid B3WG13 BK00102 is a 63% glass reinforced, injection molding, high modulus nylon designed to have high strength and stiffness for metal replacement applications. It also has excellent moldability and outstanding surface appearance.
Potential applications are mirror brackets, fuel lids, gas-assisted steering wheel inserts, ski bindings and bike rack clamps.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 高强度高刚性良好表面填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 63% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.74 g/cm³ | ISO 1183 | |
比重 | 1.74 - | ASTM D792 | |
收缩率 | |||
- | 0.2 % | Internal | 1/8" bar |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 155 Mpa | ISO 527 | Conditioned,23℃ |
断裂(brk) | 235 Mpa | ISO 527 | Dry,23℃ |
断裂(brk) | 207 Mpa | ASTM D638 | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 3 % | ASTM D638 | Dry,23℃ |
断裂(brk) | 2 % | ISO 527 | Dry,23℃ |
弯曲强度 | |||
- | 378 Mpa | ASTM D790 | Dry,23℃ |
- | 335 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 17300 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 19000 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 13400 Mpa | ISO 527 | Conditioned,23℃ |
拉伸模量 | 22000 Mpa | ISO 527 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 13 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 15 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 90 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 90 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 155 J/m | ASTM D256 | Dry |
23℃ (73℉) | 15 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 213 °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 214 °C | ISO 75 | Dry |
熔融温度(Tm) | 220 °C | ASTM D3418 | Dry |
熔融温度(Tm) | 220 °C | ISO 3146 | Dry |