Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also available in non-heat stabilized (Ultramid 8233G) and/or pigmented versions.
Applications
Ultramid 8233G HS is generally recommended for applications such as power tool housings, weed trimmer components, gears, automotive housings and under hood applications.
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 高强度高刚性耐热热稳定尺寸稳定填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 33% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.39 - | ASTM D792 | |
收缩率 | |||
- | 0.3 % | Internal | |
吸水率 | 1.1 % | ASTM D570 | 24 hr |
吸水率 | 1.8 % | ASTM D570 | 50% RH |
吸水率 | 6.4 % | ASTM D570 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 255 Mpa | ASTM D638 | Conditioned,-40℃ |
断裂(brk) | 60 Mpa | ASTM D638 | Conditioned,121℃ |
断裂(brk) | 125 Mpa | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 80 Mpa | ASTM D638 | Conditioned,80℃ |
断裂(brk) | 284 Mpa | ASTM D638 | Dry,-40℃ |
断裂(brk) | 83 Mpa | ASTM D638 | Dry,121℃ |
断裂(brk) | 195 Mpa | ASTM D638 | Dry,23℃ |
断裂(brk) | 110 Mpa | ASTM D638 | Dry,80℃ |
拉伸延伸率 | |||
断裂(brk) | 3.5 % | ASTM D638 | Conditioned,-40℃ |
断裂(brk) | 6 % | ASTM D638 | Conditioned,121℃ |
断裂(brk) | 6 % | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 6 % | ASTM D638 | Conditioned,80℃ |
断裂(brk) | 3.6 % | ASTM D638 | Dry,-40℃ |
断裂(brk) | 7 % | ASTM D638 | Dry,121℃ |
断裂(brk) | 3.5 % | ASTM D638 | Dry,23℃ |
断裂(brk) | 7 % | ASTM D638 | Dry,80℃ |
弯曲强度 | |||
- | 361 Mpa | ASTM D790 | Conditioned,-40℃ |
- | 179 Mpa | ASTM D790 | Conditioned,23℃ |
- | 380 Mpa | ASTM D790 | Dry,-40℃ |
- | 112 Mpa | ASTM D790 | Dry,121℃ |
- | 297 Mpa | ASTM D790 | Dry,23℃ |
- | 160 Mpa | ASTM D790 | Dry,65℃ |
- | 140 Mpa | ASTM D790 | Dry,90℃ |
弯曲模量 | 10200 Mpa | ASTM D790 | Conditioned,-40℃ |
弯曲模量 | 5130 Mpa | ASTM D790 | Conditioned,23℃ |
弯曲模量 | 9830 Mpa | ASTM D790 | Dry,-40℃ |
弯曲模量 | 3320 Mpa | ASTM D790 | Dry,121℃ |
弯曲模量 | 9040 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 4020 Mpa | ASTM D790 | Dry,65℃ |
弯曲模量 | 3750 Mpa | ASTM D790 | Dry,90℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 107 J/m | ASTM D256 | Conditioned |
-40℃ (-40℉) | 107 J/m | ASTM D256 | Dry |
23℃ (73℉) | 235 J/m | ASTM D256 | Conditioned |
23℃ (73℉) | 148 J/m | ASTM D256 | Dry |
落锤冲击 | 6.78 J | Internal | Conditioned,23℃ |
落锤冲击 | 4.07 J | Internal | Dry |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 121 R | ASTM D785 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 218 °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 210 °C | ASTM D648 | Dry |
相对温度指数(RTI) | |||
冲击w/impact,1.5/1.6 mm | 115 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 140 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm | 140 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
- | 38 E-6 mm/mm/℃ | ASTM D E831 | Dry |
熔融温度(Tm) | 220 °C | ASTM D3418 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | Dry,1.50 mm |