AKROMID® B3 GF 40 1 black (8353)
PA6
安科罗/开德阜(AKRO-PLASTIC)
产品描述
AKROMID® B3 GF 40 1 black (8353) is a 40% glass fiber reinforced polyamide 6 which is characterised by excellent bonding to LSR (liquid silicone rubber). Furthermore, the material shows high stiffness and strength. On top of that, it is heat stabilised and low in emissions and therefore perfectly suitable for technical applications in industrial engineering and in the automotive industry, such as airbag applications.
基本信息
原厂资料 | 物性表(英文) | |||
产品特性 | 高强度高刚性热稳定良好粘合性低挥发VOC填充增强 | |||
添加助剂 | 热稳定剂 | |||
颜色形状 | 粒状黑色 | |||
成型方式 | 注塑 | |||
增强填充 | 40% 玻纤 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.46 g/cm³ | ISO 1183 | 23°C |
收缩率 | |||
纵向(Flow) | 0.1~0.3 % | ISO 294-4 | |
横向(Across Flow) | 0.5~0.7 % | ISO 294-4 | |
吸湿率 | 1.8 % | ISO 1110 | 70°C, 62% r.H. |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 131.2 Mpa | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) | 195 Mpa | ISO 527-2 | Dry, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 3.5 % | ISO 527-2 | Dry, 5 mm/min |
弯曲强度 | |||
- | 305 Mpa | ISO 178 | Dry, 2 mm/min |
弯曲应变 | |||
断裂(brk) | 3.7 % | ISO 178 | Dry, 2 mm/min |
弯曲模量 | 12259 Mpa | ISO 178 | Dry, 2 mm/min |
拉伸模量 | 8300 Mpa | ISO 527-2 | Cond., 1 mm/min |
拉伸模量 | 13000 Mpa | ISO 527-2 | Dry, 1 mm/min |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 12 kJ/m² | ISO 179-1/1eA | Dry |
23℃ (73℉) | 23.3 kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | 16 kJ/m² | ISO 179-1/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 85 kJ/m² | ISO 179-1/1eU | Dry |
23℃ (73℉) | 115 kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | 100 kJ/m² | ISO 179-1/1eU | Dry |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 220 °C | ISO 11357-3 | DSC, 10K/min |
燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.8 mm | UL94 |