Ultramid® 8272G HS BK102
PA6
巴斯夫 (BASF)
产品描述
Ultramid 8272G HS BK102 is a 12% glass fiber reinforced, black pigmented, thermally modified, PA6 blow molding compound offering an excellent balance of engineering properties combined with the melt strength ideally suited for blow molding and other applications requiring ultra high melt viscosity. It exhibits improved strength, stiffness and creep resistance compare to standard blow molding grades. Outstanding permeability and chemical resistance to oils, hydrocarbons and most solvents are other advantages along with excellent stiffness ad the ability to fabricate complex shapes for cost effective metal replacements.
Applications
Ultramid 8272G HS BK102 is designed for blow molding applications requiring improved short term thermal performance as well as extrusions. It is ideal for air ducts, reservoirs and covers.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 抗蠕变耐化学性耐燃油耐油填充增强高阻隔性 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 挤出吹塑 | |||
| 增强填充 | 12% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.22 g/cm³ | ISO 1183 | |
比重 | 1.22 - | ASTM D792 | |
收缩率 | |||
- | 0.3 % | Internal | 3.18 mm |
吸水率 | 1.4 % | ASTM D570 | 24 hr |
吸水率 | 2.3 % | ASTM D570 | 50% RH |
吸水率 | 8.3 % | ASTM D570 | Saturation |
吸水率 | 1.4 % | ISO 62 | 24 hr |
吸水率 | 2.3 % | ISO 62 | 50% RH |
吸水率 | 8.3 % | ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 110 Mpa | ISO 527 | Conditioned,-40℃ |
断裂(brk) | 25 Mpa | ISO 527 | Conditioned,120℃ |
断裂(brk) | 25 Mpa | ISO 527 | Conditioned,150℃ |
断裂(brk) | 60 Mpa | ISO 527 | Conditioned,23℃ |
断裂(brk) | 115 Mpa | ISO 527 | Dry,-40℃ |
断裂(brk) | 45 Mpa | ISO 527 | Dry,120℃ |
断裂(brk) | 40 Mpa | ISO 527 | Dry,150℃ |
断裂(brk) | 110 Mpa | ISO 527 | Dry,23℃ |
断裂(brk) | 110 Mpa | ASTM D638 | Conditioned,-40℃ |
断裂(brk) | 25 Mpa | ASTM D638 | Conditioned,121℃ |
断裂(brk) | 60 Mpa | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 115 Mpa | ASTM D638 | Dry,-40℃ |
断裂(brk) | 45 Mpa | ASTM D638 | Dry,121℃ |
断裂(brk) | 110 Mpa | ASTM D638 | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 2 % | ASTM D638 | Conditioned,-40℃ |
断裂(brk) | 20 % | ASTM D638 | Conditioned,121℃ |
断裂(brk) | 2 % | ASTM D638 | Dry,-40℃ |
断裂(brk) | 15 % | ASTM D638 | Dry,121℃ |
断裂(brk) | 3 % | ASTM D638 | Dry,23℃ |
断裂(brk) | 2 % | ISO 527 | Conditioned,-40℃ |
断裂(brk) | 20 % | ISO 527 | Conditioned,120℃ |
断裂(brk) | 15 % | ISO 527 | Conditioned,150℃ |
断裂(brk) | 2 % | ISO 527 | Dry,-40℃ |
断裂(brk) | 15 % | ISO 527 | Dry,120℃ |
断裂(brk) | 12.5 % | ISO 527 | Dry,150℃ |
断裂(brk) | 3 % | ISO 527 | Dry,23℃ |
弯曲强度 | |||
- | 265 Mpa | ASTM D790 | Conditioned,-40℃ |
- | 80 Mpa | ASTM D790 | Conditioned,23℃ |
- | 200 Mpa | ASTM D790 | Dry,-40℃ |
- | 50 Mpa | ASTM D790 | Dry,121℃ |
- | 165 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 5580 Mpa | ASTM D790 | Conditioned,-40℃ |
弯曲模量 | 1970 Mpa | ASTM D790 | Conditioned,23℃ |
弯曲模量 | 5200 Mpa | ASTM D790 | Dry,-40℃ |
弯曲模量 | 995 Mpa | ASTM D790 | Dry,121℃ |
弯曲模量 | 4650 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 4300 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 6400 Mpa | ISO 527 | Conditioned,-40℃ |
拉伸模量 | 1500 Mpa | ISO 527 | Conditioned,120℃ |
拉伸模量 | 1400 Mpa | ISO 527 | Conditioned,150℃ |
拉伸模量 | 3100 Mpa | ISO 527 | Conditioned,23℃ |
拉伸模量 | 1900 Mpa | ISO 527 | Conditioned,80℃ |
拉伸模量 | 6370 Mpa | ISO 527 | Dry,-40℃ |
拉伸模量 | 1445 Mpa | ISO 527 | Dry,120℃ |
拉伸模量 | 1470 Mpa | ISO 527 | Dry,150℃ |
拉伸模量 | 5220 Mpa | ISO 527 | Dry,23℃ |
拉伸模量 | 2100 Mpa | ISO 527 | Dry,80℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 7.1 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 40 J/m | ASTM D256 | Conditioned |
-40℃ (-40℉) | 40 J/m | ASTM D256 | Dry |
23℃ (73℉) | 155 J/m | ASTM D256 | Conditioned |
23℃ (73℉) | 45 J/m | ASTM D256 | Dry |
23℃ (73℉) | 5.9 kJ/m² | ISO 180 | Dry |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 121 R | ASTM D785 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 210 °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 197 °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 170 °C | ISO 75 | Dry |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 28 E-6/°C | Internal | Dry |
横向(Across Flow) | 72 E-6/°C | Internal | Dry |
- | 97 E-6 mm/mm/℃ | ASTM D E831 | Dry |
熔融温度(Tm) | 220 °C | ASTM D3418 | Dry |
熔融温度(Tm) | 220 °C | ISO 3146 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | Conditioned |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | Dry,1.5 mm |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | Dry |