TECHNYL® C 50H2 BLACK 46 N
PA6
索尔维(苏威)(Solvay)
产品描述
TECHNYL® C 50H2 Black 46 N is an unreinforced polyamide 6 based on a non-phosphorous and non-halogenated flame retardant system, heat stabilized, for injection moulding. This product, UL94 VO @ 0,4mm, offers excellent moldability together with good stiffness.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃易脱模 | |||
| 添加助剂 | 阻燃剂热稳定剂 | |||
| 法规认证 | EN 45545(欧盟轨道交通防火测试)NF F 16-101(法国铁路防火测试)REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质)UL QMFZ2(UL认证) | |||
| 颜色形状 | 粒状本色黑色灰色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.16 g/cm³ | ISO 1183 | Dry |
吸水率 | 1.1 % | ISO 62 | 24 hr, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 80 Mpa | ASTM D638 | Dry,23℃ |
屈服(yld) | 50 Mpa | ISO 527-2/1A | Conditioned,23℃ |
屈服(yld) | 75 Mpa | ISO 527-2/1A | Dry,23℃ |
断裂(brk) | 80 Mpa | ASTM D638 | Dry,23℃ |
断裂(brk) | 40 Mpa | ISO 527-2/1A | Conditioned,23℃ |
断裂(brk) | 60 Mpa | ISO 527-2/1A | Dry,23℃ |
拉伸延伸率 | |||
屈服(yld) | 5 % | ISO 527-2 | Conditioned,23℃ |
屈服(yld) | 3.5 % | ISO 527-2 | Dry,23℃ |
断裂(brk) | 15 % | ASTM D638 | Dry,23℃ |
断裂(brk) | 38 % | ISO 527-2 | Conditioned,23℃ |
断裂(brk) | 25 % | ISO 527-2 | Dry,23℃ |
弯曲强度 | |||
- | 115 Mpa | ASTM D790 | Dry,23℃ |
- | 70 Mpa | ISO 178 | Conditioned,23℃ |
- | 200 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 3500 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 2000 Mpa | ISO 178 | Conditioned,23℃ |
弯曲模量 | 3150 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 2000 Mpa | ISO 527-2/1A | Conditioned,23℃ |
拉伸模量 | 3500 Mpa | ISO 527-2/1A | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 15 kJ/m² | ISO 179/1eA | Conditioned |
23℃ (73℉) | 6 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 180 kJ/m² | ISO 179/1eU | Dry |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 65 J/m | ASTM D256 | Dry |
23℃ (73℉) | 15 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | 3.5 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 75 °C | ASTM D648 | Dry,Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 75 °C | ISO 75-2/Af | Dry,Unannealed |
熔融温度(Tm) | 222 °C | ISO 11357-3 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.4 mm | UL94 | Dry |
V-0 | 0.8 mm | UL94 | Dry |
V-0 | 1.6 mm | UL94 | Dry |
V-0 | 3.2 mm | UL94 | Dry |
氧指数(LOI) | 36 % | ISO 4589 | Dry |
灼热丝可燃性指数(GWFI) | |||
0.8mm | 960 °C | IEC 60695-2-12 | Dry |
1.6mm | 960 °C | IEC 60695-2-12 | Dry |
3.2mm | 960 °C | IEC 60695-2-12 | Dry |
灼热丝点燃温度(GWIT) | |||
0.8mm | 700 °C | IEC 60695-2-13 | Dry |
1.6mm | 700 °C | IEC 60695-2-13 | Dry |
3.2mm | 700 °C | IEC 60695-2-13 | Dry |
欧洲轨道车辆认证 | 3 HL | EN 45545-2 | R22 |
欧洲轨道车辆认证 | 3 HL | EN 45545-2 | R23 |
欧洲轨道车辆认证 | 3 HL | EN 45545-2 | R25 |
法国轨道车辆认证 | F2 - | NF F16-101 | French Fire Index |
法国轨道车辆认证 | I2 - | NF F16-101 | French Smoke Index |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+12 Ohm-cm | IEC 60093 | Conditioned |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | Dry |
表面电阻率 | 1.0E+12 Ohm | IEC 60093 | Conditioned |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | Dry |
介电常数(DK) | |||
- | 3.9 - | IEC 60250 | Conditioned |
- | 3.5 - | IEC 60250 | Dry |
耗散因数(DF) | |||
- | 600 E-4 | IEC 60250 | Conditioned |
- | 200 E-4 | IEC 60250 | Dry |
相比漏电起痕指数(CTI ) | |||
溶液A | 600 V | IEC 60112 | Conditioned |
溶液A | 600 V | IEC 60112 | Dry |
溶液B | 475 V | IEC 60112 | Dry |
绝缘强度 | 30 kV/mm | IEC 60243-1 | Conditioned,2.00mm |
绝缘强度 | 34 kV/mm | IEC 60243-1 | Dry,2.00mm |