TECHNYL® C 256 V18 (EX PSB 197)
PA6
索尔维(苏威)(Solvay)
产品描述
TECHNYL® C 256 V18 Natural is a polyamide PA 6 impact modified, reinforced with 18% of glass fibre, for injection moulding. This grade offers high impact strength and good mechanical properties.
基本信息
原厂资料 | 物性表(英文) | |||
产品特性 | 高冲击易脱模填充增强 | |||
添加助剂 | 抗冲击剂热稳定剂 | |||
法规认证 | REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质) | |||
颜色形状 | 粒状本色黑色 | |||
成型方式 | 注塑 | |||
增强填充 | 18% 玻纤 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.23 g/cm³ | ISO 1183 | Dry |
收缩率 | |||
纵向(Flow) | 0.3 % | ISO 294-4 | Dry |
横向(Across Flow) | 0.85 % | ISO 294-4 | Dry |
吸水率 | 2.4 % | ISO 62 | Equilibrium, 23°C, 50% RH |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 70 Mpa | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 110 Mpa | ASTM D638 | Dry,23℃ |
断裂(brk) | 70 Mpa | ISO 527-2/1A | Conditioned,23℃ |
断裂(brk) | 120 Mpa | ISO 527-2/1A | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 10 % | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 3.6 % | ASTM D638 | Dry,23℃ |
断裂(brk) | 8.7 % | ISO 527-2 | Conditioned,23℃ |
断裂(brk) | 3.5 % | ISO 527-2 | Dry,23℃ |
弯曲模量 | 3000 Mpa | ISO 178 | Conditioned,23℃ |
弯曲模量 | 5500 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 3300 Mpa | ISO 527-2/1A | Conditioned,23℃ |
拉伸模量 | 6000 Mpa | ISO 527-2/1A | Dry,23℃ |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 7.5 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 20 kJ/m² | ISO 179/1eA | Conditioned |
23℃ (73℉) | 13 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 80 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 80 kJ/m² | ISO 179/1eU | Conditioned |
23℃ (73℉) | 75 kJ/m² | ISO 179/1eU | Dry |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 13 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | 22 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | 13 kJ/m² | ISO 180 | Dry |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 80 kJ/m² | ASTM D256 | Conditioned |
23℃ (73℉) | 75 kJ/m² | ASTM D256 | Dry |
23℃ (73℉) | 65 kJ/m² | ISO 180/1U | Conditioned |
23℃ (73℉) | 60 kJ/m² | ISO 180/1U | Dry |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)(4.6kg/cm²) | 215 °C | ISO 75-2/Bf | Dry,Unannealed |
1.8 Mpa (264 psi)(18.6kg/cm²) | 192 °C | ISO 75-2/Af | Dry,Unannealed |
熔融温度(Tm) | 222 °C | ISO 11357-3 | Dry |
燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | UL94 | Dry |