Ultramid® 8333G HI HS BK102
PA6
巴斯夫 (BASF)
产品描述
Ultramid® 8333G HI HS BK102 is a 33% glass reinforced, impact modified PA6 injection molding compound pigmented black developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics.
Ultramid® 8333G HI HS BK102 is generally recommended for application such as front wheel chair wheels, bicycle wheels, power tool housings, chain saw housings, clips and fasteners, hose clamps and window hardware.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性良好表面填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 应用产品 | 轮椅前轮子自行车车轮链锯外壳夹子紧固件软管卡箍窗户配件 | |||
| 增强填充 | 33% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.34 g/cm³ | ISO 1183 | |
吸水率 | 0.9 % | ISO 62 | 24 h in water, 23 °C |
吸水率 | 5.5 % | ISO 62 | equilibrium in water at 23°C |
吸湿率 | 1.5 % | ISO 62 | equilibrium 23°C/50% r.h. |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 137 Mpa | ISO 527-1/-2 | Dry, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 2.4 % | ISO 527-1/-2 | Dry, 50 mm/min |
弯曲强度 | |||
- | 210 Mpa | ISO 178 | Dry |
弯曲模量 | 8460 Mpa | ISO 178 | Dry |
拉伸模量 | 9250 Mpa | ISO 527-1/-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 15 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 68 kJ/m² | ISO 179/1eU | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 13 kJ/m² | ISO 180/A | Dry |
23℃ (73℉) | 16 kJ/m² | ISO 180/A | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 220 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 201 °C | ISO 75-1/-2 | |
相对温度指数(RTI) | |||
冲击w/impact,0.8mm | 115 °C | UL 746B | |
冲击w/impact,1.5/1.6 mm | 120 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm | 130 °C | UL 746B | |
电气Elec,0.8mm | 140 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 140 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 140 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm | 140 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm | 140 °C | UL 746B | |
熔融温度(Tm) | 217 °C | ISO 11357-1/-3 | DSC |
加工温度 | 270~295 °C | - | Injection moulding/Extrusion |
模具温度 | 80~95 °C | - | Injection moulding |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.81 mm | IEC 60695-11-10 | |
HB | 1.5 mm | IEC 60695-11-10 | |
HB | 3 mm | IEC 60695-11-10 | |
HB | 3 mm | IEC 60695-11-10 |