Orgalloy® R60 ES NAT
PA6 Alloy
阿科玛 (Arkema)
产品描述
Orgalloy® polyamide alloys combine the important physical and chemical properties of short-chain polyamides with the economic and process advantages of polyolefins. They are designed to offer improved dimensional stability, lower density and better mechanical properties than PA 6 and PA 6.6 resins.
Orgalloy® R 60 ES NAT resin is a polyamide alloy especially designed for blown film extrusion. This natural grade dedicated to extrusion offers good barrier properties and chemical resistance to solvents and alcohols while exhibiting a low surface tension (easy release).
Main applications:
Technical film for Sheet Molding Compound (SMC).
Packaging:
This grade is delivered dried in sealed packaging (800kg octabin) ready to be processed.
Shelf life:
Two years from the date of delivery. For any use above this limit, please refer to our technical services.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 尺寸稳定易脱模抗紫外线耐化学性耐酒精耐溶剂高阻隔性 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 挤出薄膜挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.03 g/cm³ | ISO 1183 | Cond. |
密度 | 1.03 g/cm³ | ISO 1183 | Dry |
熔体体积流动速率(MVR) | |||
235℃/2.16 kg | 2.5 cm³/10 min | ISO 1133 | Dry |
吸水率 | 3.3 % | ISO 62 | Dry |
吸湿率 | 1.3 % | ISO 62 | Dry |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 50 Mpa | ISO 527-1/-2 | Cond. |
拉伸延伸率 | |||
屈服(yld) | 3.4 % | ISO 527-1/-2 | Cond. |
标称断裂伸长率 | 50 % | ISO 527-1/-2 | Cond. |
拉伸模量 | 1950 Mpa | ISO 527-1/-2 | Cond. |
拉伸蠕变模量 | |||
1h | 2030 Mpa | ISO 899-1 | Cond. |
1000h | 870 Mpa | ISO 899-1 | Cond. |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 9 kJ/m² | ISO 179/1eA | Cond. |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Cond. |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 73 D | ISO 7619-1 | 15s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 130 °C | ISO 75-1/-2 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 75 °C | ISO 75-1/-2 | Dry |
维卡软化温度(Vicat) | 134 °C | ISO 306 | Dry, 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 93 E-6/K | ISO 11359-1/-2 | Dry |
横向(Across Flow) | 133 E-6/K | ISO 11359-1/-2 | Dry |
熔融温度(Tm) | 220 °C | ISO 11357-1/-3 | Dry, 10°C/min |
加工温度 | 260 °C | - | Injection Molding |
模具温度 | 60 °C | - | Injection Molding |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | IEC 60695-11-10 | Dry |
HB | 3.2 mm | IEC 60695-11-10 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | Cond. |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | Cond. |
介电常数(DK) | |||
100Hz | 3 - | IEC 60250 | Cond. |
1MHz | 3 - | IEC 60250 | Cond. |
耗散因数(DF) | |||
100Hz | 620 E-4 | IEC 60250 | Cond. |
1MHz | 250 E-4 | IEC 60250 | Cond. |
相比漏电起痕指数(CTI ) | |||
- | 600 - | IEC 60112 | Cond. |
绝缘强度 | 38 kV/mm | IEC 60243-1 | Cond. |
绝缘强度 | 38 kV/mm | IEC 60243-1 | Dry |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 33 Mpa | ISO 527-3 | normal |
屈服(yld) | 35 Mpa | ISO 527-3 | parallel |
断裂(brk) | 60 Mpa | ISO 527-3 | normal |
断裂(brk) | 80 Mpa | ISO 527-3 | parallel |
拉伸延伸率 | |||
屈服(yld) | 15 % | ISO 527-3 | normal |
屈服(yld) | 20 % | ISO 527-3 | parallel |
断裂(brk) | 530 % | ISO 527-3 | normal |
断裂(brk) | 530 % | ISO 527-3 | parallel |
裤形撕裂 | 35 N | ISO 6383-2 | normal |
裤形撕裂 | 40 N | ISO 6383-2 | parallel |
氧渗透 | 170 cm³/m²/bar/24 hr | DIS 15105-1/-2 | 23°C, 0% RH |
氧渗透 | 170 cm³/m²/bar/24 hr | DIS 15105-1/-2 | 23°C, 85% RH |
原材料现货供应: