AKROMID® B3 GF 50 S1 black (2000)
PA6
安科罗/开德阜(AKRO-PLASTIC)
产品描述
AKROMID® B3 GF 50 S1 black 950089 (2000) is a 50% glass fiber reinforced, impact modified Polyamide 6. It is characterised by very high stiffness and strength as well as a higher notched impact strength compared to a standard PA 6 GF 50. The material is therefore perfectly suitable for industrial applications and for housings and covers in the automotive industry.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性高冲击增韧/冲击改性填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 50% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.54 g/cm³ | ISO 1183 | 23°C |
收缩率 | |||
纵向(Flow) | 0.1~0.3 % | ISO 294-4 | |
横向(Across Flow) | 0.4~0.6 % | ISO 294-4 | |
吸湿率 | 1.3 % | ISO 1110 | 70°C, 62% r.H. |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 120 Mpa | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) | 190 Mpa | ISO 527-2 | Dry, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 8 % | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) | 5 % | ISO 527-2 | Dry, 5 mm/min |
拉伸模量 | 7800 Mpa | ISO 527-2 | Cond., 1 mm/min |
拉伸模量 | 15000 Mpa | ISO 527-2 | Dry, 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 20 kJ/m² | ISO 179-1/1eA | Cond. |
-30℃ (-22℉) | 20 kJ/m² | ISO 179-1/1eA | Dry |
23℃ (73℉) | 40 kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | 25 kJ/m² | ISO 179-1/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 100 kJ/m² | ISO 179-1/1eU | Dry |
23℃ (73℉) | NB kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | 100 kJ/m² | ISO 179-1/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 210 °C | ISO 75/A | |
熔融温度(Tm) | 222 °C | ISO 11357-3 | DSC, 10K/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | UL94 | |
FMVSS | + pass | FMVSS 302 | > 1 mm Thickness |