LNP™ THERMOCOMP™ PF007S
PA6
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP PF007S is a compound based on Nylon 6 resin containing 35% Glass Fiber. Added feature of this material is: Heat Stabilized.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 增强填充 | 35% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.45 g/cm³ | ASTM D792 | |
比重 | 1.45 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.2~0.4 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.8~1 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 1.6 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 1 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 162 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 167 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 2 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 1.9 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
断裂(brk) | 236 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 211 Mpa | ISO 178 | |
弯曲模量 | 10600 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 10270 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 11860 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 11540 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 80 J/m | ASTM D256 | |
23℃ (73℉) | 7 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 724 J/m | ASTM D4812 | |
23℃ (73℉) | 43 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 9 J | ASTM D3763 | |
多轴冲击 | 2 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 218 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 217 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 209 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 205 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 2 E-6/°C | ASTM D 696 | -30°C to 30°C, flow |
横向(Across Flow) | 6 E-6/°C | ASTM D 696 | -30°C to 30°C, xflow |