Ultramid® B3M6 BK60564
PA6
巴斯夫 (BASF)
产品描述
Ultramid B3M6 BK60564 is a 30% mineral reinforced, pigmented black injection molding PA6 grade for industrial items requiring high impact strength and very high dimensional stability, excellent laser markability.
Applications
Typical applications include industrial items.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 高刚性高冲击印刷/标记填充增强 | |||
| 增强填充 | 30% 矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.36 g/cm³ | ISO 1183 | |
比重 | 1.36 - | ASTM D792 | |
收缩率 | |||
- | 0.9 % | Internal | 1/8" bar |
吸水率 | 2.4 % | ASTM D570 | 50% RH |
吸水率 | 6.2 % | ASTM D570 | Saturation |
吸水率 | 2.4 % | ISO 62 | 50% RH |
吸水率 | 6.2 % | ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 85 Mpa | ISO 527 | Dry,23℃ |
断裂(brk) | 85 Mpa | ASTM D638 | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 4.9 % | ASTM D638 | Dry,23℃ |
断裂(brk) | 4.9 % | ISO 527 | Dry,23℃ |
弯曲模量 | 3270 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 3700 Mpa | ISO 527 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 5.6 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 45 J/m | ASTM D256 | Dry |
-40℃ (-40℉) | 4 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | 64 J/m | ASTM D256 | Dry |
23℃ (73℉) | 5.5 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 195 °C | ASTM D648 | Dry |
0.45 Mpa (66 psi)（4.6kg/cm²） | 160 °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 120 °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 70 °C | ISO 75 | Dry |
熔融温度(Tm) | 220 °C | ASTM D3418 | Dry |
熔融温度(Tm) | 220 °C | ISO 3146 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | Dry |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | Dry,1.5 mm |