TECHNYL® C 548B V15 BLACK
TECHNYL® C 548B V15 BLACK
PA6
索尔维(苏威)(Solvay)
产品描述
TECHNYL® C 548B V15 Black is a polyamide 6, reinforced with 15% of glass fiber, high viscosity, for extrusion blow-moulding. This grade offers an optimal processing behavior in blow moulding processes (2D, 3D, suction blow moulding). Specific features are high barrier properties especially to fuels and oils, heat stability up to 170°C, dimensional stability in temperature as well as excellent surface aspect.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 高冲击热稳定耐燃油耐油高粘度高熔体强度填充增强高阻隔性 |
| 添加助剂 | 抗冲击剂热稳定剂 |
| 法规认证 | REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质) |
| 颜色形状 | 粒状黑色 |
| 成型方式 | 吹塑 |
| 增强填充 | 15% 玻纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.18 g/cm³
| ISO 1183 | Dry |
吸水率 | 1.4 %
| ISO 62 | 24 hr,23℃ |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
70 Mpa | ISO 527-2/1A | Conditioned,23℃ |
断裂(brk) |
85 Mpa | ISO 527-2/1A | Dry,23℃ |
拉伸延伸率 | | | |
断裂(brk) |
3 % | ISO 527-2 | Dry,23℃ |
拉伸模量 | 3800 Mpa
| ISO 527-2/1A | Conditioned,23℃ |
拉伸模量 | 5000 Mpa
| ISO 527-2/1A | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
22 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) |
14 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
185 °C | ISO 75-2/Bf | Dry,Unannealed |
熔融温度(Tm) | 222 °C
| ISO 11357-3 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
1.6 mm | UL94 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-cm
| IEC 60093 | Conditioned |
体积电阻率 | 1.0E+15 Ohm-cm
| IEC 60093 | Dry |
表面电阻率 | 1.0E+12 Ohm
| IEC 60093 | Conditioned |
表面电阻率 | 1.0E+14 Ohm
| IEC 60093 | Dry |
介电常数(DK) | | | |
- |
4 - | IEC 60250 | Conditioned |
- |
3.7 - | IEC 60250 | Dry |
耗散因数(DF) | | | |
- |
1200 E-4 | IEC 60250 | Conditioned |
- |
200 E-4 | IEC 60250 | Dry |
绝缘强度 | 21 kV/mm
| IEC 60243-1 | Conditioned,2.00mm |
原材料现货供应:133-8218-6680(微信同号)