Ultramid® B3WGM45 SW106B
PA6
巴斯夫 (BASF)
产品描述
Pigmented black, heat and UV stabilised, 45 % glass and mineral fibre reinforced polyamide 6 injection moulding compound. It possesses a balance of engineering properties in combination with excellent dimensional stability, low warp and resistance to sink-mark-formation. It is ideally suited for applications such as rotors, wheels, rims, timing belt covers, automotive cooling fans, shrouds as well as interior and exterior door handles.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定尺寸稳定低翘曲抗紫外线填充增强 | |||
| 添加助剂 | 紫外线稳定剂热稳定剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 20% 玻纤25% 矿物45% 玻纤+矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.51 g/cm³ | ISO 1183 | |
粘度 | 145 cm³/g | ISO 307, 1157, 1628 | 0.5% in 96% H2SO4 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 140 Mpa | ISO 527-1/-2 | Dry |
拉伸延伸率 | |||
断裂(brk) | 2 % | ISO 527-1/-2 | Dry |
弯曲强度 | |||
- | 210 Mpa | ISO 178 | Dry |
弯曲模量 | 8900 Mpa | ISO 178 | Dry |
拉伸模量 | 10000 Mpa | ISO 527-1/-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 6 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 50 kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 215 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 200 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 220 °C | ISO 11357-1/-3 | DSC |
加工温度 | 250~295 °C | - | Injection moulding/Extrusion |
模具温度 | 80~95 °C | - | Injection moulding |