Ultramid® 8202C HS BK102
PA6
巴斯夫 (BASF)
产品描述
Ultramid 8202C HS BK102 is a heat stabilized, low viscosity, pigmented black, PA6, injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also available in non-heat stabilized (Ultramid 8202C).
Applications
Ultramid 8202C HS BK102 is generally recommended for applications such as gears, valves, fittings, insulators, bushings, slides, window hardware, wiring devices, textile components and furniture casters.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 热稳定短周期成型低粘度 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.13 g/cm³ | ISO 1183 | |
比重 | 1.13 - | ASTM D792 | |
收缩率 | |||
- | 0.9 % | Internal | 3.18 mm |
吸水率 | 1.6 % | ASTM D570 | 24 hr |
吸水率 | 2.6 % | ASTM D570 | 50% RH |
吸水率 | 9.3 % | ASTM D570 | Saturation |
吸水率 | 1.6 % | ISO 62 | 24 hr |
吸水率 | 2.6 % | ISO 62 | 50% RH |
吸水率 | 9.3 % | ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 142 Mpa | ASTM D638 | Conditioned,-40℃ |
屈服(yld) | 25 Mpa | ASTM D638 | Conditioned,121℃ |
屈服(yld) | 48 Mpa | ASTM D638 | Conditioned,23℃ |
屈服(yld) | 30 Mpa | ASTM D638 | Conditioned,80℃ |
屈服(yld) | 137 Mpa | ASTM D638 | Dry,-40℃ |
屈服(yld) | 30 Mpa | ASTM D638 | Dry,121℃ |
屈服(yld) | 90 Mpa | ASTM D638 | Dry,23℃ |
屈服(yld) | 40 Mpa | ASTM D638 | Dry,80℃ |
屈服(yld) | 43 Mpa | ISO 527 | Conditioned,23℃ |
屈服(yld) | 85 Mpa | ISO 527 | Dry,23℃ |
断裂(brk) | 80 Mpa | ASTM D638 | Conditioned,-40℃ |
断裂(brk) | 20 Mpa | ASTM D638 | Conditioned,121℃ |
断裂(brk) | 70 Mpa | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 30 Mpa | ASTM D638 | Conditioned,80℃ |
断裂(brk) | 130 Mpa | ASTM D638 | Dry,-40℃ |
断裂(brk) | 25 Mpa | ASTM D638 | Dry,121℃ |
断裂(brk) | 90 Mpa | ASTM D638 | Dry,23℃ |
断裂(brk) | 35 Mpa | ASTM D638 | Dry,80℃ |
拉伸延伸率 | |||
屈服(yld) | 3 % | ASTM D638 | Conditioned,-40℃ |
屈服(yld) | 30 % | ASTM D638 | Conditioned,121℃ |
屈服(yld) | 22 % | ASTM D638 | Conditioned,23℃ |
屈服(yld) | 25 % | ASTM D638 | Conditioned,80℃ |
屈服(yld) | 3 % | ASTM D638 | Dry,-40℃ |
屈服(yld) | 27 % | ASTM D638 | Dry,121℃ |
屈服(yld) | 4 % | ASTM D638 | Dry,23℃ |
屈服(yld) | 25 % | ASTM D638 | Dry,80℃ |
屈服(yld) | 22 % | ISO 527 | Conditioned,23℃ |
屈服(yld) | 4 % | ISO 527 | Dry,23℃ |
断裂(brk) | 3 % | ASTM D638 | Conditioned,-40℃ |
断裂(brk) | 100 % | ASTM D638 | Conditioned,121℃ |
断裂(brk) | 100 % | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 100 % | ASTM D638 | Conditioned,80℃ |
断裂(brk) | 5 % | ASTM D638 | Dry,-40℃ |
断裂(brk) | 100 % | ASTM D638 | Dry,121℃ |
断裂(brk) | 12 % | ASTM D638 | Dry,23℃ |
断裂(brk) | 100 % | ASTM D638 | Dry,80℃ |
标称断裂伸长率 | 50 % | ISO 527 | Conditioned,23℃ |
标称断裂伸长率 | 10 % | ISO 527 | Dry,23℃ |
弯曲强度 | |||
- | 168 Mpa | ASTM D790 | Conditioned,-40℃ |
- | 42 Mpa | ASTM D790 | Conditioned,23℃ |
- | 183 Mpa | ASTM D790 | Dry,-40℃ |
- | 21 Mpa | ASTM D790 | Dry,121℃ |
- | 110 Mpa | ASTM D790 | Dry,23℃ |
- | 30 Mpa | ASTM D790 | Dry,65℃ |
- | 95 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 4200 Mpa | ASTM D790 | Conditioned,-40℃ |
弯曲模量 | 970 Mpa | ASTM D790 | Conditioned,23℃ |
弯曲模量 | 3370 Mpa | ASTM D790 | Dry,-40℃ |
弯曲模量 | 385 Mpa | ASTM D790 | Dry,121℃ |
弯曲模量 | 3170 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 600 Mpa | ASTM D790 | Dry,65℃ |
弯曲模量 | 440 Mpa | ASTM D790 | Dry,90℃ |
弯曲模量 | 2800 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 1360 Mpa | ISO 527 | Conditioned,23℃ |
拉伸模量 | 3500 Mpa | ISO 527 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 3 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 21 J/m | ASTM D256 | Conditioned |
-40℃ (-40℉) | 32 J/m | ASTM D256 | Dry |
23℃ (73℉) | 171 J/m | ASTM D256 | Conditioned |
23℃ (73℉) | 48 J/m | ASTM D256 | Dry |
落锤冲击 | 271 J | Internal | Conditioned,23℃ |
落锤冲击 | 122 J | Internal | Dry,23℃ |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 120 R | ASTM D785 | Dry |
球压硬度 | 200 Mpa | ISO 2039-1 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 190 °C | ASTM D648 | Dry |
0.45 Mpa (66 psi)（4.6kg/cm²） | 160 °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 75 °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 60 °C | ISO 75 | Dry |
相对温度指数(RTI) | |||
冲击w/impact,0.71mm | 95 °C | UL 746B | |
冲击w/impact,1.5/1.6 mm | 105 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm | 105 °C | UL 746B | |
冲击w/impact,6.0mm | 105 °C | UL 746B | |
电气Elec,0.71mm | 130 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 130 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 130 °C | UL 746B | |
电气Elec,6.0mm | 130 °C | UL 746B | |
强度w/o impact,0.71mm | 95 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm | 105 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm | 105 °C | UL 746B | |
强度w/o impact,6.0mm | 105 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
- | 81 E-6 mm/mm/℃ | ASTM D E831 | Dry |
熔融温度(Tm) | 220 °C | ASTM D3418 | Dry |
熔融温度(Tm) | 220 °C | ISO 3146 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.71 mm | UL94 | |
V-2 | 1.5 mm | UL94 | |
V-2 | 3 mm | UL94 | |
V-2 | 6 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | Dry,1.5 mm |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | Dry |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | Dry |