Durethan® BM40XH2.0EF 900116
PA6
朗盛 (LANXESS)
产品描述
PA 6, 40 % glass fibers/mineral, injection molding, improved flowability, heat-aging stabilized, low tendency to warp, improved surface finish
ISO Shortname: ISO 16396-PA 6,(GF+MD)40,GHR,S10-080
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐热老化良好表面低翘曲高流动填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 40% 玻纤+矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.45 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.31 % | ISO 294-4 | 0x60x2; 290℃/MT80℃;600 bar |
纵向(Flow) | 0.05 % | ISO 294-4 | 60x60x2; 120℃; 4 h |
纵向(Flow) | 0.05 % | ISO 2577 | 150x105x3;120℃;4 h |
纵向(Flow) | 0.25 % | ISO 2577 | 150x105x3;290℃/MT 80℃;500 bar |
横向(Across Flow) | 0.72 % | ISO 294-4 | 0x60x2; 290℃/MT80℃;600 bar |
横向(Across Flow) | 0.11 % | ISO 294-4 | 60x60x2; 120℃; 4 h |
横向(Across Flow) | 0.15 % | ISO 2577 | 150x105x3;120℃;4 h |
横向(Across Flow) | 0.87 % | ISO 2577 | 150x105x3;290℃/MT 80℃;500 bar |
吸水率 | 1.7 % | ISO 62 | Equilibrium, 23°C, 50% RH |
吸水率 | 5.8 % | ISO 62 | Saturation, 23°C |
堆积(视)密度 | 0.7 g/cm³ | ISO 60 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 125 Mpa | ISO 527-1/-2 | Dry,5mm/min |
断裂(brk) | 65 Mpa | ISO 527-1/-2 | cond. ,5mm/min |
拉伸延伸率 | |||
断裂(brk) | 2.5 % | ISO 527-1/-2 | Dry,5mm/min |
断裂(brk) | 8.7 % | ISO 527-1/-2 | cond. ,5mm/min |
弯曲强度 | |||
3.5%应变 | 200 Mpa | ISO 178/A | Dry,2mm/min |
3.5%应变 | 110 Mpa | ISO 178/A | cond. ,2mm/min |
- | 206 Mpa | ISO 178/A | Dry,2mm/min |
- | 125 Mpa | ISO 178/A | cond. ,2mm/min |
弯曲应变 | |||
- | 2.9 % | ISO 178/A | Dry,2mm/min |
- | 6.2 % | ISO 178/A | cond. ,2mm/min |
弯曲模量 | 8800 Mpa | ISO 178/A | Dry,2mm/min |
弯曲模量 | 4250 Mpa | ISO 178/A | cond. ,2mm/min |
拉伸模量 | 9000 Mpa | ISO 527-1/-2 | Dry,1mm/min |
拉伸模量 | 4500 Mpa | ISO 527-1/-2 | cond. ,1mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 179/1eA | Dry |
-30℃ (-22℉) | 10 kJ/m² | ISO 179/1eA | cond. |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | cond. |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 37 kJ/m² | ISO 179/1eU | Dry |
-30℃ (-22℉) | 45 kJ/m² | ISO 179/1eU | cond. |
23℃ (73℉) | 40 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 65 kJ/m² | ISO 179/1eU | cond. |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 180/1A | Dry |
-30℃ (-22℉) | 10 kJ/m² | ISO 180/1A | cond. |
23℃ (73℉) | 10 kJ/m² | ISO 180/1A | Dry |
23℃ (73℉) | 10 kJ/m² | ISO 180/1A | cond. |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | 33 kJ/m² | ISO 180/1U | Dry |
-30℃ (-22℉) | 30 kJ/m² | ISO 180/1U | cond. |
23℃ (73℉) | 35 kJ/m² | ISO 180/1U | Dry |
23℃ (73℉) | 60 kJ/m² | ISO 180/1U | cond. |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 210 Mpa | ISO 2039-1 | Dry |
球压硬度 | 95 Mpa | ISO 2039-1 | cond. |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 215 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 195 °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 28 E-6/K | ISO 11359-1/-2 | 23 to 55℃ |
横向(Across Flow) | 85 E-6/K | ISO 11359-1/-2 | 23 to 55℃ |
熔融温度(Tm) | 220 °C | ISO 11357-1/-3 | 10℃/min |
加工温度 | 290 °C | - | Injection molding |
模具温度 | 80 °C | - | Injection molding |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | |
HB | 1.5 mm | UL94 |