SCHULAMID® 6 GF 15 FR 4 K1681
SCHULAMID® 6 GF 15 FR 4 K1681
PA6
利安德巴塞尔(LyondellBasell)
产品描述
15% glass fibre reinforced flame-retardant Polyamide 6 grade without PBDE
基本信息
| 原厂资料 | 物性表-ISO(英文) |
| 产品特性 | 阻燃不含多溴联苯填充增强 |
| 成型方式 | 注塑 |
| 增强填充 | 15% 玻纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.38 g/cm³
| ISO 1183 | |
收缩率 | | | |
纵向(Flow) |
0.3 % | ISO 294-4 | |
横向(Across Flow) |
0.8 % | ISO 294-4 | |
粘度 | 145 cm³/g
| ISO 307 | Viscosity Number |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
117 Mpa | ISO 527-2/1A/5 | |
断裂(brk) |
71 Mpa | ISO 527-2/1A/5 | Conditioned |
拉伸延伸率 | | | |
断裂(brk) |
3.5 % | ISO 527-2/1A/5 | |
断裂(brk) |
8.5 % | ISO 527-2/1A/5 | Conditioned |
拉伸模量 | 7100 Mpa
| ISO 527-2/1A/1 | |
拉伸模量 | 4000 Mpa
| ISO 527-2/1A/1 | Conditioned |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
6 kJ/m² | ISO 179/1eA | |
23℃ (73℉) |
9 kJ/m² | ISO 179/1eA | |
23℃ (73℉) |
14 kJ/m² | ISO 179/1eA | Conditioned |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
55 kJ/m² | ISO 179/1eU | |
23℃ (73℉) |
60 kJ/m² | ISO 179/1eU | |
23℃ (73℉) |
70 kJ/m² | ISO 179/1eU | Conditioned |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
223 °C | ISO 75-2/Bf | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
203 °C | ISO 75-2/Af | Unannealed |
相对温度指数(RTI) | | | |
冲击w/impact,0.36/0.4mm |
75 °C | UL 746 | |
冲击w/impact,0.75/0.8mm |
90 °C | UL 746 | |
冲击w/impact,1.5/1.6 mm |
100 °C | UL 746 | |
冲击w/impact,3.0/3.2 mm |
100 °C | UL 746 | |
电气Elec,0.36/0.4mm |
130 °C | UL 746 | |
电气Elec,0.75/0.8mm |
130 °C | UL 746 | |
电气Elec,1.5/1.6 mm |
120 °C | UL 746 | |
电气Elec,1.5/1.6 mm |
130 °C | UL 746 | |
电气Elec,3.0/3.2 mm |
130 °C | UL 746 | |
强度w/o impact,0.36/0.4mm |
100 °C | UL 746 | |
强度w/o impact,0.75/0.8mm |
110 °C | UL 746 | |
强度w/o impact,3.0/3.2 mm |
120 °C | UL 746 | |
球压痕温度 | 200 °C
| IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
V-2 |
0.38 mm | UL94 | |
V-2 |
0.75 mm | UL94 | |
V-2 |
1.5 mm | UL94 | |
V-2 |
3 mm | UL94 | |
氧指数(LOI) | 26 %
| ISO 4589 | |
灼热丝可燃性指数(GWFI) | | | |
0.38mm |
850 °C | IEC 60695-2-12 | |
0.75mm |
960 °C | IEC 60695-2-12 | |
1.5mm |
960 °C | IEC 60695-2-12 | |
3mm |
960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | | | |
0.38mm |
825 °C | IEC 60695-2-13 | |
0.75mm |
900 °C | IEC 60695-2-13 | |
1.5mm |
900 °C | IEC 60695-2-13 | |
3.0mm |
900 °C | IEC 60695-2-13 | |
燃烧速率 | 0 mm/min
| ISO 3795 | 0.38 mm, Self-Extinguishing |
燃烧速率 | 0 mm/min
| ISO 3795 | 0.75 mm, Self-Extinguishing |
燃烧速率 | 0 mm/min
| ISO 3795 | 1.50 mm, Self-Extinguishing |
燃烧速率 | 0 mm/min
| ISO 3795 | 3.00 mm, Self-Extinguishing |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m
| IEC 62631-3-1 | |
体积电阻率 | 1.0E+10 Ohm-m
| IEC 62631-3-1 | Conditioned |
表面电阻率 | 1.0E+15 Ohm
| IEC 60093 | |
相比漏电起痕指数(CTI ) | | | |
- |
275 V | IEC 60112 | |
热线圈起燃性(HWI) | 3 PLC
| UL 746 | 0.38 mm |
热线圈起燃性(HWI) | 0 PLC
| UL 746 | 0.75 mm |
热线圈起燃性(HWI) | 0 PLC
| UL 746 | 1.5 mm |
热线圈起燃性(HWI) | 0 PLC
| UL 746 | 3.0 mm |
高电流弧起燃性(HAI) | 0 PLC
| UL 746 | 0.38 mm |
高电流弧起燃性(HAI) | 0 PLC
| UL 746 | 0.75 mm |
高电流弧起燃性(HAI) | 0 PLC
| UL 746 | 1.5 mm |
高电流弧起燃性(HAI) | 0 PLC
| UL 746 | 3.0 mm |