AKROMID® B3 GF 15 S3 black (2345)
AKROMID® B3 GF 15 S3 black (2345)
PA6
安科罗/开德阜(AKRO-PLASTIC)
产品描述
AKROMID® B3 GF 15 S3 black (2345) is a
15% glass fiber reinforced, impact modified
Polyamide 6. It is characterised by medium
stiffness and strength as well as a higher
impact strength compared to a standard PA
6 GF 15. It also has good surface properties.
The material is therefore perfectly suitable
for toughness demanding but high
integrated parts with a good surface
appearance in the automotive, electro, and
furniture industry.
基本信息
原厂资料 | 物性表(英文) |
产品特性 | 增韧/冲击改性良好表面填充增强 |
添加助剂 | 抗冲击剂 |
颜色形状 | 粒状黑色 |
成型方式 | 注塑 |
增强填充 | 15% 玻纤 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.21 g/cm³
| ISO 1183 | 23°C |
熔体体积流动速率(MVR) | | | |
275°C/5 kg |
45 cm³/10 min | ISO 1133 | |
收缩率 | | | |
纵向(Flow) |
0.2~0.4 % | ISO 294-4 | |
横向(Across Flow) |
0.6~0.8 % | ISO 294-4 | |
吸湿率 | 2.3~2.6 %
| ISO 1110 | 70°C, 62% r.H. |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
75 Mpa | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) |
110 Mpa | ISO 527-2 | Dry, 5 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
15 % | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) |
4 % | ISO 527-2 | Dry, 5 mm/min |
拉伸模量 | 3000 Mpa
| ISO 527-2 | Cond., 1 mm/min |
拉伸模量 | 5500 Mpa
| ISO 527-2 | Dry, 1 mm/min |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
6 kJ/m² | ISO 179-1/1eA | Dry |
23℃ (73℉) |
20 kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) |
14 kJ/m² | ISO 179-1/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
50 kJ/m² | ISO 179-1/1eU | Dry |
23℃ (73℉) |
100 kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) |
75 kJ/m² | ISO 179-1/1eU | Dry |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)(18.6kg/cm²) |
216 °C | ISO 75/A | |
熔融温度(Tm) | 225 °C
| ISO 11357-3 | DSC, 10K/min |
燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
1.6 mm | UL94 | |
FMVSS | + pass
| FMVSS 302 | > 1 mm Thickness |