Ultramid® B3WG3 BK23274
PA6
巴斯夫 (BASF)
产品描述
ISO 1874-PA6 MNHS 14-050 GF15
Injection moulding grade, glass fibre-reinforced, heat stabilized, easy flowing, technical moulded parts with high rigidity and dimensional stability for use in construction of vehicles, electrical engineering, machine construction, building trade and in the field of leisure time articles
Application:
door handles, control elements, housing for relays, fans, radiator grill
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定尺寸稳定良好流动性填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 15% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.24 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.53 % | ISO 294-4 | |
横向(Across Flow) | 0.83 % | ISO 294-4 | |
吸水率 | 8.2~8.7 % | ISO 62 | saturation in water at 23°C |
吸湿率 | 2 % | ISO 62 | equilibrium 23°C/50% r.h. |
粘度 | 145 cm³/g | ISO 307, 1157, 1628 | 0.5% in 96% H2SO4 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 75 Mpa | ISO 527-1/-2 | Cond. |
断裂(brk) | 120 Mpa | ISO 527-1/-2 | Dry |
拉伸延伸率 | |||
断裂(brk) | 10 % | ISO 527-1/-2 | Cond. |
断裂(brk) | 2.6 % | ISO 527-1/-2 | Dry |
弯曲强度 | |||
- | 180 Mpa | ISO 178 | Dry |
弯曲模量 | 4500 Mpa | ISO 178 | Dry |
拉伸模量 | 3200 Mpa | ISO 527-1/-2 | Cond. |
拉伸模量 | 6000 Mpa | ISO 527-1/-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 3.5 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 4 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 30 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 35 kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 210 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 190 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 220 °C | ISO 11357-1/-3 | DSC |
加工温度 | 270~290 °C | - | Injection moulding/Extrusion |
模具温度 | 80~90 °C | - | Injection moulding |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
FMVSS | + pass | FMVSS 302 | Thickness ≥ 1 mm |
燃烧速率 | + mm/min | ISO 3795 | Thickness ≥ 1 mm |