| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.31 g/cm³
| DIN 53479 | Dry |
收缩率 | | | |
- |
2 % | ISO 294-4 | Dry |
填充/灰分 | 25 %
| ISO 3451 | Dry |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
52 Mpa | ISO 527-2/5 | Cond. |
断裂(brk) |
58 Mpa | ISO 527-2/5 | Dry, 23°C, 4.00 mm, Injection Molded |
拉伸延伸率 | | | |
断裂(brk) |
10 % | ISO 527-2/5 | Cond. |
断裂(brk) |
8.7 % | ISO 527-2/5 | Dry, 23°C, 4.00 mm, Injection Molded |
拉伸模量 | 4000 Mpa
| ISO 527-2/1 | Cond. |
拉伸模量 | 4300 Mpa
| ISO 527-2/1 | Dry, 23°C, 4.00 mm, Injection Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
3 kJ/m² | ISO 179 | Dry, Injection Molded |
23℃ (73℉) |
4.4 kJ/m² | ISO 179 | Cond. |
23℃ (73℉) |
2.7 kJ/m² | ISO 179 | Dry, Injection Molded |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
19 kJ/m² | ISO 179 | Dry, Injection Molded |
23℃ (73℉) |
32 kJ/m² | ISO 179 | Cond. |
23℃ (73℉) |
28 kJ/m² | ISO 179 | Dry, Injection Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
205 °C | ISO 75-2/B | Unannealed |
熔融温度(Tm) | 233 °C
| ISO 3146 | DSC |
连续使用温度 | | | |
- |
95 °C | IEC 60216 | |
短周期使用温度 | 190 °C
| IEC 60216 | GTP 50% Tensile |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-cm
| IEC 60093 | Cond. |
体积电阻率 | 1.0E+15 Ohm-cm
| IEC 60093 | Dry |
表面电阻率 | 1.0E+12 Ohm
| IEC 60093 | Cond. |
表面电阻率 | 1.0E+14 Ohm
| IEC 60093 | Dry |