AKROMID® B3 1 FR orange (7698)
AKROMID® B3 1 FR orange (7698)
PA6
安科罗/开德阜(AKRO-PLASTIC)
产品描述
AKROMID® B3 1 FR orange (7698) is an unreinforced, flame retardant and heat stabilised PA6, colored in orange (similar RAL 2003). Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade meets the requirements for public transportation (EN 45545-2) and is also suitable for housing, fasteners and cable connectors in the E&E markets.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 热稳定阻燃无卤无红磷良好表面良好流动性 |
| 添加助剂 | 阻燃剂热稳定剂 |
| 法规认证 | EN 45545(欧盟轨道交通防火测试) |
| 颜色形状 | 粒状橙色 |
| 成型方式 | 注塑 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.19 g/cm³
| ISO 1183 | |
收缩率 | | | |
纵向(Flow) |
0.9~1.1 % | ISO 294-4 | |
横向(Across Flow) |
1~1.2 % | ISO 294 | |
吸湿率 | 2.3~2.5 %
| ISO 1110 | 70°C, 62% r.H. |
螺旋流 | 160 mm
| - | 1mm Thickness |
螺旋流 | 460 mm
| - | 2mm Thickness |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
45 Mpa | ISO 527-2 | Cond., 50 mm/min |
屈服(yld) |
75 Mpa | ISO 527-2 | Dry, 50 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
50 % | ISO 527-2 | Cond., 50 mm/min |
断裂(brk) |
10 % | ISO 527-2 | Dry, 50 mm/min |
拉伸模量 | 1400 Mpa
| ISO 527-2 | Cond., 1 mm/min |
拉伸模量 | 3600 Mpa
| ISO 527-2 | Dry, 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
23℃ (73℉) |
13 kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) |
4.5 kJ/m² | ISO 179-1/1eA | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
180 °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
60 °C | ISO 75/A | |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
78 E-6/K | ISO 11359-1/-2 | 23°C to 80°C |
横向(Across Flow) |
78 E-6/K | ISO 11359-1/-2 | 23°C to 80°C |
熔融温度(Tm) | 222 °C
| ISO 11357-3 | DSC, 10K/min |
导热系数 | 0.33 W/(m K)
| DIN 52612-1 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
V-0 |
0.4 mm | UL94 | |
V-0 |
0.8 mm | UL94 | |
V-0 |
1.6 mm | UL94 | |
V-0 |
3.2 mm | UL94 | |
氧指数(LOI) | 32 %
| ISO 4589 | |
灼热丝可燃性指数(GWFI) | | | |
0.4mm |
960 °C | IEC 60695-2-12 | |
0.8mm |
960 °C | IEC 60695-2-12 | |
1.6mm |
960 °C | IEC 60695-2-12 | |
3.2mm |
960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | | | |
0.4 mm |
775 °C | IEC 60695-2-13 | |
0.8mm |
750 °C | IEC 60695-2-13 | |
1.6mm |
750 °C | IEC 60695-2-13 | |
3.2mm |
775 °C | IEC 60695-2-13 | |
欧洲轨道车辆认证 | 3 HL
| EN 45545-2 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | | | |
溶液A |
600 V | IEC 60112 | |
绝缘强度 | 10 kV/mm
| IEC 60243 | 3 mm |
热线圈起燃性(HWI) | 4 PLC
| UL 746A | 0,4mm |
热线圈起燃性(HWI) | 4 PLC
| UL 746A | 0,8mm |
热线圈起燃性(HWI) | 0 PLC
| UL 746A | 1,6mm |
热线圈起燃性(HWI) | 0 PLC
| UL 746A | 3,2mm |
高电流弧起燃性(HAI) | 0 PLC
| UL 746A | 0,4mm |
高电流弧起燃性(HAI) | 0 PLC
| UL 746A | 0,8mm |
高电流弧起燃性(HAI) | 0 PLC
| UL 746A | 1,6mm |
高电流弧起燃性(HAI) | 0 PLC
| UL 746A | 3,2mm |