PA6 Alloy Orgalloy® LT 5050 T6L NAT

Orgalloy® LT 5050 T6L NAT

Orgalloy® LT 5050 T6L NAT

PA6 Alloy

阿科玛 (Arkema)

产品描述

Orgalloy® polyamide alloys combine the important physical and chemical properties of short-chain polyamides with the economic and process advantages of polyolefins. They are designed to offer improved dimensional stability, lower density and better mechanical properties than PA 6 and PA 6.6 resins.

Orgalloy® LT 5050 T6L NAT resin is a polyamide alloy especially designed for tube extrusion. This natural grade dedicated to extrusion offers good barrier properties and chemical resistance to oils and HFC gas, a high thermal resistance and flexibility.
Main applications:

  • Barrier layer for air conditioning hoses.

  • Barrier layer for LPG lines.

    Packaging:
    This grade is delivered dried in sealed packaging (25kg bags) ready to be processed.
    Shelf life:
    Two years from the date of delivery. For any use above this limit, please refer to our technical services.

    基本信息
    原厂资料
    物性表(英文)
    产品特性
    耐热
    热稳定
    尺寸稳定
    抗紫外线
    耐化学性
    耐油
    高阻隔性
    添加助剂
    紫外线稳定剂
    热稳定剂
    颜色形状
    粒状
    本色
    成型方式
    压延
    树脂转移模塑(RTM)
    挤出
    片材挤出
    型材挤出
    薄膜挤出
    热成型
    技术参数
    物理性能 值/单位 测试标准 测试条件

    密度

    1.04 g/cm³ ISO 1183
    Cond.

    密度

    1.04 g/cm³ ISO 1183
    Dry

    熔体体积流动速率(MVR)

    235°C/5.0 kg

    2.5 cm³/10 min ISO 1133
    Dry
    机械性能 值/单位 测试标准 测试条件

    拉伸强度

    50%延伸率时

    23 Mpa ISO 527-1/-2
    Cond.

    拉伸延伸率

    断裂(brk)

    50 % ISO 527-1/-2
    Cond.

    拉伸模量

    500 Mpa ISO 527-1/-2
    Cond.

    拉伸蠕变模量

    1h

    420 Mpa ISO 899-1
    Cond.

    1000h

    270 Mpa ISO 899-1
    Cond.
    冲击性能 值/单位 测试标准 测试条件

    简支梁缺口(Charpy Notched)

    23℃ (73℉)

    80 kJ/m² ISO 179/1eA
    Cond.

    23℃ (73℉)

    75 kJ/m² ISO 179/1eA
    Dry

    简支梁无缺口(Charpy Unnotched)

    23℃ (73℉)

    NB kJ/m² ISO 179/1eU
    Cond.

    23℃ (73℉)

    NB kJ/m² ISO 179/1eU
    Dry
    硬度性能 值/单位 测试标准 测试条件

    邵氏硬度 D

    55 D ISO 7619-1
    15s
    热学性能 值/单位 测试标准 测试条件

    维卡软化温度(Vicat)

    75 °C ISO 306
    Dry, 50°C/h 50N

    线性膨胀系数(CLTE)

    纵向(Flow)

    170 E-6/K ISO 11359-1/-2
    Dry

    横向(Across Flow)

    180 E-6/K ISO 11359-1/-2
    Dry

    熔融温度(Tm)

    220 °C ISO 11357-1/-3
    Dry, 10°C/min

    加工温度

    260 °C -
    Injection Molding

    模具温度

    60 °C -
    Injection Molding
    燃烧性能 值/单位 测试标准 测试条件

    UL 防火等级

    HB

    1.6 mm IEC 60695-11-10
    Dry

    HB

    3.2 mm IEC 60695-11-10
    Dry
    电学性能 值/单位 测试标准 测试条件

    体积电阻率

    7.5E+11 Ohm-m IEC 60093
    Cond.

    表面电阻率

    1.0E+15 Ohm IEC 60093
    Cond.

    介电常数(DK)

    100Hz

    4 - IEC 60250
    Cond.

    1MHz

    4 - IEC 60250
    Cond.

    耗散因数(DF)

    100Hz

    1100 E-4 IEC 60250
    Cond.

    1MHz

    500 E-4 IEC 60250
    Cond.

    相比漏电起痕指数(CTI )

    -

    600 - IEC 60112
    Cond.

    绝缘强度

    36 kV/mm IEC 60243-1
    Cond.

    绝缘强度

    36 kV/mm IEC 60243-1
    Dry