LNP™ THERMOTUF™ PF006I
PA6
沙特基础 (SABIC)
产品描述
LNP THERMOTUF* PF006I is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: High Impact.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击填充增强 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.37 g/cm³ | ISO 1183 | |
密度 | 1.35 g/cm³ | ASTM D792 | |
比重 | 1.35 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.11~0.3 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 0.1~0.3 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.9~0.2 % | ASTM D 955 | xflow, 24 hrs |
横向(Across Flow) | 0.62~0.67 % | ISO 294 | xflow, 24 hrs |
吸湿率 | 0.83 % | ISO 62 | |
吸湿率 | 0.83 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 50 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 35 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 99 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 97 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 8.1 % | ASTM D638 | Type I, 5 mm/min |
弯曲强度 | |||
断裂(brk) | 157 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 6820 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 16230 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 9650 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 106 J/m | ASTM D256 | |
23℃ (73℉) | 10 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 727 J/m | ASTM D4812 | |
23℃ (73℉) | 53 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 16 J | ASTM D3763 | |
多轴冲击 | 4 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 139 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 141 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 137 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 135 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 |