Ultramid® C3U
PA6
巴斯夫 (BASF)
产品描述
Ultramid C3U is an injection molding, general purpose PA6/66 grade with improved flame retardance. The product is UL recognized as 94V0 at 0.4 mm minimum thickness.
Applications
It is used for impact resistant electrical insulating parts such as contact bases and plug connector strips.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 高冲击阻燃绝缘 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.16 g/cm³ | ISO 1183 | |
比重 | 1.16 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
275°C/5 kg | 140 cm³/10 min | ISO 1133 | |
收缩率 | |||
- | 0.8 % | Internal | 1/8" bar |
吸水率 | 2.9 % | ASTM D570 | 50% RH |
吸水率 | 8.5 % | ASTM D570 | Saturation |
吸水率 | 2.9 % | ISO 62 | 50% RH |
吸水率 | 8.5 % | ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 83 Mpa | ASTM D638 | Dry,23℃ |
屈服(yld) | 45 Mpa | ISO 527 | Conditioned,23℃ |
屈服(yld) | 75 Mpa | ISO 527 | Dry,23℃ |
拉伸延伸率 | |||
屈服(yld) | 5 % | ASTM D638 | Dry,23℃ |
屈服(yld) | 18 % | ISO 527 | Conditioned,23℃ |
屈服(yld) | 4 % | ISO 527 | Dry,23℃ |
断裂(brk) | 50 % | ASTM D638 | Dry,23℃ |
标称断裂伸长率 | 5.7 % | ISO 527 | Conditioned,-40℃ |
标称断裂伸长率 | 50 % | ISO 527 | Conditioned,23℃ |
标称断裂伸长率 | 4.4 % | ISO 527 | Dry,-40℃ |
标称断裂伸长率 | 6 % | ISO 527 | Dry,23℃ |
弯曲模量 | 3000 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 3000 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 1500 Mpa | ISO 527 | Conditioned,23℃ |
拉伸模量 | 3500 Mpa | ISO 527 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 35 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 9 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 80 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 32 J/m | ASTM D256 | Dry |
23℃ (73℉) | 43 J/m | ASTM D256 | Dry |
23℃ (73℉) | 4.5 kJ/m² | ISO 180 | Dry |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 100 Mpa | ISO 2039-1 | Dry,23℃ |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 224 °C | ASTM D648 | Dry |
0.45 Mpa (66 psi)（4.6kg/cm²） | 210 °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 91 °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 70 °C | ISO 75 | Dry |
相对温度指数(RTI) | |||
冲击w/impact,0.36/0.4mm | 65 °C | UL 746B | |
冲击w/impact,0.75/0.8mm | 105 °C | UL 746B | |
冲击w/impact,1.5/1.6 mm | 105 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm | 105 °C | UL 746B | |
电气Elec,0.36/0.4mm | 110 °C | UL 746B | |
电气Elec,0.75/0.8mm | 120 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 120 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 120 °C | UL 746B | |
强度w/o impact,0.36/0.4mm | 65 °C | UL 746B | |
强度w/o impact,0.75/0.8mm | 115 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm | 120 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm | 120 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 80 E-6/°C | Internal | Dry |
横向(Across Flow) | 90 E-6/°C | Internal | Dry |
- | 40 E-6 mm/mm/℃ | ASTM D E831 | Dry |
熔融温度(Tm) | 243 °C | ASTM D3418 | Dry |
熔融温度(Tm) | 243 °C | ISO 3146 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.38 mm | UL94 | |
V-0 | 0.75 mm | UL94 | |
V-0 | 1.5 mm | UL94 | |
V-0 | 3 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+9 Ohm-m | ASTM D257 | Conditioned,1.50 mm |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | Dry,1.50 mm |
体积电阻率 | 1.0E+9 Ohm-m | IEC 60093 | Conditioned |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | Dry |
介电常数(DK) | |||
1MHz | 6 - | IEC 60250 | Conditioned |
1MHz | 3.6 - | IEC 60250 | Dry |
耗散因数(DF) | |||
1MHz | 3000 E-4 | IEC 60250 | Conditioned |
1MHz | 200 E-4 | IEC 60250 | Dry |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | Conditioned |
- | 600 V | IEC 60112 | Dry |
绝缘强度 | 28 kV/mm | IEC 60243-1 | Conditioned |
绝缘强度 | 32 kV/mm | IEC 60243-1 | Dry |