AKROMID® B28 GF 35 FR EN black (7484)
PA6
安科罗/开德阜(AKRO-PLASTIC)
产品描述
AKROMID® B28 GF 35 FR EN black (7484) is an easy flowing PA6 with 35% glass-fibers and flame retardant free of halogens and red phosporous. The product contains an organic stabilization package and is optimized for use in electronic and electric applications.
This formulation has been listed at UL under the name AKROMID® B28 GF 35 9 FR black (8189). Please consider AKROMID® B28 GF 35 9 FR black (8189), in case EN quality is not explicitly necessary, because EN requires additional effort and testing.
Typical applications
circuit breaker and housings in E&E industry.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无卤无红磷填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 35% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.46 g/cm³ | ISO 1183 | 23°C |
收缩率 | |||
纵向(Flow) | 0.1~0.3 % | ISO 294-4 | |
横向(Across Flow) | 0.4~0.6 % | ISO 294 | |
吸湿率 | 1.6~1.8 % | ISO 1110 | 70°C, 62% r.H. |
螺旋流 | 380 mm | - | 2mm Thickness |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 108 Mpa | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) | 152 Mpa | ISO 527-2 | Dry, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 4 % | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) | 2.6 % | ISO 527-2 | Dry, 5 mm/min |
弯曲强度 | |||
- | 179 Mpa | ISO 178 | Cond., 2 mm/min |
- | 240 Mpa | ISO 178 | Dry, 2 mm/min |
弯曲模量 | 9000 Mpa | ISO 178 | Cond., 2 mm/min |
弯曲模量 | 11800 Mpa | ISO 178 | Dry, 2 mm/min |
拉伸模量 | 8300 Mpa | ISO 527-2 | Cond., 1 mm/min |
拉伸模量 | 12600 Mpa | ISO 527-2 | Dry, 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 11 kJ/m² | ISO 179-1/1eA | Dry |
23℃ (73℉) | 14 kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | 12 kJ/m² | ISO 179-1/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 70 kJ/m² | ISO 179-1/1eU | Dry |
23℃ (73℉) | 70 kJ/m² | ISO 179-1/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 222 °C | ISO 11357-3 | DSC, 10K/min |
温度指数(TI)-拉伸强度 | |||
5000 h | 165 °C | IEC 60216 | 50% loss of tensile strength |
20000 h | 135 °C | IEC 60216 | 50% loss of tensile strength |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.6 mm | UL94 | |
V-0 | 3.2 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
0.8mm | 960 °C | IEC 60695-2-12 | |
1.6mm | 850 °C | IEC 60695-2-12 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 4.0E+13 Ohm-cm | IEC 60093 | Dry |
体积电阻率 | 4.0E+13 Ohm-cm | IEC 62631-3-1 | Dry |
表面电阻率 | 3.9E+11 Ohm | IEC 62631-3-2 | Dry |
相比漏电起痕指数(CTI ) | |||
溶液A | 600 V | IEC 60112 |