LNP™ THERMOTUF™ VF004S
PA (尼龙-聚酰胺)
沙特基础 (SABIC)
产品描述
LNP THERMOTUF* VF004S is a compound based on Super Tough Nylon resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高韧性热稳定填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 增强填充 | 20% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.23 g/cm³ | ISO 1183 | |
密度 | 1.23 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.4~0.6 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.8~1 % | ASTM D 955 | xflow, 24 hrs |
吸湿率 | 1.1 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.74 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 97 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 102 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 2.8 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 2.6 % | ISO 527 | 5 mm/min |
断裂(brk) | 3 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 3 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
断裂(brk) | 156 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 5620 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 5080 Mpa | ISO 178 | |
拉伸模量 | 6470 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 6000 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 128 J/m | ASTM D256 | |
23℃ (73℉) | 12 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 704 J/m | ASTM D4812 | |
23℃ (73℉) | 42 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 22 J | ASTM D3763 | |
多轴冲击 | 6 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 256 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 235 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 240 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 235 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 299 E-6/°C | ASTM E831 | -30°C to 30°C, flow |
横向(Across Flow) | 812 E-6/°C | ASTM E831 | -30°C to 30°C, xflow |