TROGAMID® T5002
PA (尼龙-聚酰胺)
赢创(原德固赛)(Evonik)
产品描述
TROGAMID® T5002 is an amorphous polyamide with high toughness, good resistance to chemicals compared to other amorphous plastics and suitable for injection molding and extrusion.
Because of its amorphous character, TROGAMID® T5002 shows a very low mold shrinkage and warpage.
TROGAMID® T5002 is supplied as cylindrical pellets in moisture-proof packaging, ready for processing.
Pigmentation may affect values.
Industrial Sector
Automotive, Electrical and Electronical, Instustry and Building Construction
Applications
IT and Telecommunication
Processing
Injection Molding, Film Extrusion, Profile Extrusion, Sheet Extrusion, Other Extrusion, Blow Molding
Special Characteristics
Transparent
Features
Amorphous
Delivery form
Pellets, Granules
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高韧性低翘曲耐化学性 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出片材挤出型材挤出薄膜挤出吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.12 g/cm³ | ISO 1183 | dry |
熔体体积流动速率(MVR) | |||
300°C/5.0 kg | 18.9 cm³/10 min | ISO 1133 | dry |
收缩率 | |||
纵向(Flow) | 0.5 % | ISO 294-4, 2577 | dry |
横向(Across Flow) | 0.5 % | ISO 294-4, 2577 | dry |
吸水率 | 7.5 % | ISO 62 | dry |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 90 Mpa | ISO 527 | dry |
拉伸延伸率 | |||
屈服(yld) | 8 % | ISO 527 | dry |
标称断裂伸长率 | 50 % | ISO 527 | dry |
弯曲模量 | 3000 Mpa | ISO 178 | dry, 23°C |
拉伸模量 | 2800 Mpa | ISO 527 | dry |
拉伸蠕变模量 | |||
1h | 2500 Mpa | ISO 899-1 | cond., 0,5% Strain |
1000h | 1300 Mpa | ISO 899-1 | cond., 0,5% Strain |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 6 kJ/m² | ISO 179/1eA | dry |
0℃ (32℉) | 9 kJ/m² | ISO 179/1eA | dry |
23℃ (73℉) | 9 kJ/m² | ISO 179/1eA | dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | dry |
0℃ (32℉) | NB kJ/m² | ISO 179/1eU | dry |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | dry |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 86 D | ISO 7619-1 | dry, 3s |
球压硬度 | 155 Mpa | ISO 2039-1 | dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 145 °C | ISO 75-1/-2 | dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 130 °C | ISO 75-1/-2 | dry |
维卡软化温度(Vicat) | 155 °C | ISO 306 | dry, 10 N, 50 K/h |
维卡软化温度(Vicat) | 150 °C | ISO 306 | dry, 50 N, 50 K/h |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 55 E-6/K | ISO 11359-1/-2 | dry, 23°C to 55 °C |
横向(Across Flow) | 55 E-6/K | ISO 11359-1/-2 | dry, 23°C to 55 °C |
玻璃化温度(Tg) | 150 °C | ISO 11357-1/-2 | dry, 20°C/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.8 mm | IEC 60695-11-10 | dry |
V-2 | 1.6 mm | IEC 60695-11-10 | dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 62631-3-1 | dry |
表面电阻率 | 1.0E+14 Ohm | IEC 62631-3-2 | dry, A |
表面电阻率 | 1.0E+13 Ohm | IEC 62631-3-2 | dry, RSD |
介电常数(DK) | |||
100Hz | 4 - | IEC 62631-2-1 | dry |
1MHz | 3.7 - | IEC 62631-2-1 | dry |
耗散因数(DF) | |||
100Hz | 200 E-4 | IEC 62631-2-1 | dry |
1MHz | 260 E-4 | IEC 62631-2-1 | dry |
相比漏电起痕指数(CTI ) | |||
溶液A | 575 V | IEC 60112 | dry, 100 drops value |
溶液A | 600 V | IEC 60112 | dry, 50 drops value |
绝缘强度 | 26 kV/mm | IEC 60243-1 | dry, S20/P50 |