AKROMID® C28 GF 25 FRT natural (7332)
AKROMID® C28 GF 25 FRT natural (7332)
PA (尼龙-聚酰胺)
安科罗/开德阜(AKRO-PLASTIC)
产品描述
C28 GF 25 FRT natural (7332) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications and certified to EN 45545-2 R6 and EN 45545-2 R1. To achieve an excellent surface quality a mould temperature of at least 120°C is necessary. Tested according to NFPA 130.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 阻燃无卤无红磷良好表面良好流动性填充增强 |
| 添加助剂 | 阻燃剂 |
| 法规认证 | EN 45545(欧盟轨道交通防火测试) |
| 颜色形状 | 粒状本色 |
| 成型方式 | 注塑 |
| 增强填充 | 25% 玻纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.43 g/cm³
| ISO 1183 | 23°C |
收缩率 | | | |
纵向(Flow) |
0.2 % | ISO 294-4 | |
横向(Across Flow) |
0.1~0.3 % | ISO 294-4 | |
吸湿率 | 0.9~1.1 %
| ISO 1110 | 70°C, 62% r.H. |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
152 Mpa | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) |
157 Mpa | ISO 527-2 | Dry, 5 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
2.5 % | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) |
2.3 % | ISO 527-2 | Dry, 5 mm/min |
拉伸模量 | 11000 Mpa
| ISO 527-2 | Cond., 1 mm/min |
拉伸模量 | 10800 Mpa
| ISO 527-2 | Dry, 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | | | |
23℃ (73℉) |
64 kJ/m² | ISO 179-1/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
20 E-6/K | ISO 11359-1/-2 | 23°C to 80°C |
横向(Across Flow) |
66 E-6/K | ISO 11359-1/-2 | 23°C to 80°C |
熔融温度(Tm) | 238 °C
| ISO 11357-3 | DSC, 10K/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
V-0 |
0.4 mm | UL94 | |
V-0 |
0.8 mm | UL94 | |
V-0 |
1.6 mm | UL94 | |
V-0 |
3.2 mm | UL94 | |
5VA |
1.6 mm | UL94 | |
5VA |
3.2 mm | UL94 | |
灼热丝可燃性指数(GWFI) | | | |
0.4mm |
960 °C | IEC 60695-2-12 | |
0.8mm |
960 °C | IEC 60695-2-12 | |
1.6mm |
960 °C | IEC 60695-2-12 | |
3.2mm |
960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | | | |
0.4 mm |
825 °C | IEC 60695-2-13 | |
0.8mm |
800 °C | IEC 60695-2-13 | |
1.6mm |
800 °C | IEC 60695-2-13 | |
3.2mm |
850 °C | IEC 60695-2-13 | |
FMVSS | + pass
| FMVSS 302 | > 1 mm Thickness |
欧洲轨道车辆认证 | 2 HL
| EN 45545-2 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | | | |
溶液A |
600 V | IEC 60112 | |