TROGAMID® T5000
PA (尼龙-聚酰胺)
赢创(原德固赛)(Evonik)
产品描述
TROGAMID® T5000 is a transparent, amorphous polyamide with a light transmission of more than 85%, suitable for injection molding and extrusion.
Because of its amorphous character, TROGAMID® T5000 shows a very low mold shrinkage and warpage.
TROGAMID® T5000 is supplied as spherical pellets in moisture-proof packaging, ready for processing.
Industrial Sector
Automotive, Electrical and Electronical, Instustry and Building Construction, Medical, Optical industry
Applications
Encapsulation, General Purpose, IT and Telecommunication, Monofilament, Water contact
Processing
Injection Molding, Film Extrusion, Profile Extrusion, Sheet Extrusion, Other Extrusion, Blow Molding
Special Characteristics
Transparent, X-ray opaque, halogen-free, phosphorus-free, PTFE-free, High impact strength or impact modified, Non-corrosive, Food approval FDA 21 CFR
Features
Amorphous, Cut Through Resistance, Ductile, Fatigue Resistance, Thermal Stability, Weldable
Color
Natural Color
Additives
Release agent
Delivery form
Spherical Pellets
Chemical Resistance
General Chemical Resistance, Grease Resistance, Oil Resistance
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐疲劳高冲击高韧性热稳定无卤无红磷易焊接食品接触级耐化学性耐油 | |||
| 添加助剂 | 抗冲击剂脱模剂 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 颜色形状 | 粒状本色透明 | |||
| 成型方式 | 注塑挤出片材挤出型材挤出薄膜挤出吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.12 g/cm³ | ISO 1183 | dry |
熔体体积流动速率(MVR) | |||
300°C/5.0 kg | 5 cm³/10 min | ISO 1133 | dry |
收缩率 | |||
纵向(Flow) | 0.5 % | ISO 294-4, 2577 | dry |
横向(Across Flow) | 0.6 % | ISO 294-4, 2577 | dry |
吸水率 | 7.5 % | ISO 62 | dry |
熔体密度 | 950 g/cm³ | - | dry, melt |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 87 Mpa | ISO 527 | cond. |
屈服(yld) | 90 Mpa | ISO 527 | dry |
断裂(brk) | 51 Mpa | ISO 527 | cond. |
拉伸延伸率 | |||
屈服(yld) | 8 % | ISO 527 | cond. |
屈服(yld) | 8 % | ISO 527 | dry |
断裂(brk) | 20 % | ISO 527 | cond. |
标称断裂伸长率 | 20 % | ISO 527 | cond. |
标称断裂伸长率 | 50 % | ISO 527 | dry |
弯曲模量 | 3000 Mpa | ISO 178 | dry, 23°C |
拉伸模量 | 2400 Mpa | ISO 527 | cond. |
拉伸模量 | 2800 Mpa | ISO 527 | dry |
拉伸蠕变模量 | |||
1h | 2300 Mpa | ISO 899-1 | cond., 0,5% Strain |
1000h | 1100 Mpa | ISO 899-1 | cond., 0,5% Strain |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 7 kJ/m² | ISO 179/1eA | dry |
0℃ (32℉) | 11 kJ/m² | ISO 179/1eA | dry |
23℃ (73℉) | 9 kJ/m² | ISO 179/1eA | cond. |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | dry |
0℃ (32℉) | NB kJ/m² | ISO 179/1eU | dry |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | dry |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 87 D | ISO 7619-1 | dry, 3s |
球压硬度 | 175 Mpa | ISO 2039-1 | dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 145 °C | ISO 75-1/-2 | dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 130 °C | ISO 75-1/-2 | dry |
维卡软化温度(Vicat) | 155 °C | ISO 306 | dry, 10 N, 50 K/h |
维卡软化温度(Vicat) | 150 °C | ISO 306 | dry, 50 N, 50 K/h |
比热容 | 2200 J/kg-K | - | dry, melt |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 55 E-6/K | ISO 11359-1/-2 | dry, 23°C to 55 °C |
横向(Across Flow) | 55 E-6/K | ISO 11359-1/-2 | dry, 23°C to 55 °C |
玻璃化温度(Tg) | 150 °C | ISO 11357-1/-2 | dry, 20°C/min |
导热系数 | 0.21 W/(m K) | - | dry, melt |
加工温度 | 150 °C | - | dry, Ejection |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.8 mm | IEC 60695-11-10 | dry |
V-2 | 1.6 mm | IEC 60695-11-10 | dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 62631-3-1 | dry |
表面电阻率 | 1.0E+14 Ohm | IEC 62631-3-2 | dry, A |
表面电阻率 | 1.0E+13 Ohm | IEC 62631-3-2 | dry, RSA |
介电常数(DK) | |||
100Hz | 4.6 - | IEC 62631-2-1 | dry |
1MHz | 3.4 - | IEC 62631-2-1 | dry |
耗散因数(DF) | |||
100Hz | 250 E-4 | IEC 62631-2-1 | dry |
1MHz | 280 E-4 | IEC 62631-2-1 | dry |
相比漏电起痕指数(CTI ) | |||
溶液A | 575 V | IEC 60112 | dry, 100 drops value |
溶液A | 600 V | IEC 60112 | dry, 50 drops value |
绝缘强度 | 26 kV/mm | IEC 60243-1 | dry, S20/P50 |