Rilsan® Clear G820 Rnew®
PA (尼龙-聚酰胺)
阿科玛 (Arkema)
产品描述
Rilsan® Clear G820 Rnew® is a high performance transparent polyamide with outstanding chemical resistance and stress cracking resistance.This grade has been designed for injection molding applications.
Percentage of renewable carbon according to ASTM D 6866: 64-66%.
Main applications:
- Optic.
- Electonics.
- Domestic appliances.
Packaging:
This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.
Shelf Life:
Two years from the delivery. For any use above this limit, please refer to our technical services.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 生物基含可再生资源ESCR耐化学性 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1 g/cm³ | ISO 1183 | Dry |
熔体体积流动速率(MVR) | |||
275°C/2.16 kg | 8 cm³/10 min | ISO 1133 | Dry |
收缩率 | |||
纵向(Flow) | 0.2 % | ISO 294-4, 2577 | Dry |
横向(Across Flow) | 0.4 % | ISO 294-4, 2577 | Dry |
生物基(可再生碳)含量 | 64~66 % | ASTM 6866 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 66 Mpa | ISO 527-1/-2 | Cond. |
拉伸延伸率 | |||
屈服(yld) | 7 % | ISO 527-1/-2 | Cond. |
标称断裂伸长率 | 50 % | ISO 527-1/-2 | Cond. |
拉伸模量 | 1665 Mpa | ISO 527-1/-2 | Cond. |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 9 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | 6 kJ/m² | ISO 179/1eA | Cond. |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Cond. |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 76 D | ISO 7619-1 | 15s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 85 °C | ISO 75-1/-2 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 73 °C | ISO 75-1/-2 | Dry |
熔融温度(Tm) | 101 °C | ISO 11357-1/-3 | Dry, 10°C/min |
加工温度 | 280 °C | - | Injection Molding |
模具温度 | 40 °C | - | Injection Molding |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ISO 13468 | Dry |