Rilsan® Clear G170
PA (尼龙-聚酰胺)
阿科玛 (Arkema)
产品描述
Rilsan® Clear G170 is a high performance transparent polyamide with outstanding thermal resistance. This grade has been designed for extrusion and injection molding applications.
Main applications:
Coffee machine.
Fuel filter container.
Inner layer of fiber optic and copper telephone cables resistant to rodents.
Power cables resistant to rodents.
Note: This grade is not recommended by Arkema for usage in medical application. For such applications Rilsan® Clear G 170 MED should be used.
Packaging:
This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.
Shelf Life:
Two years from the delivery. For any use above this limit, please refer to our technical services.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐热 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.05 g/cm³ | ISO 1183 | Cond. |
密度 | 1.05 g/cm³ | ISO 1183 | Dry |
熔体体积流动速率(MVR) | |||
275°C/2.16 kg | 2 cm³/10 min | ISO 1133 | Dry |
收缩率 | |||
纵向(Flow) | 0.7 % | ISO 294-4, 2577 | Dry |
横向(Across Flow) | 0.7 % | ISO 294-4, 2577 | Dry |
吸水率 | 3.8 % | ISO 62 | Dry |
吸湿率 | 1.7 % | ISO 62 | Dry |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 74 Mpa | ISO 527-1/-2 | Cond. |
屈服(yld) | 76 Mpa | ISO 527-1/-2 | Dry |
拉伸延伸率 | |||
屈服(yld) | 9 % | ISO 527-1/-2 | Cond. |
屈服(yld) | 8 % | ISO 527-1/-2 | Dry |
标称断裂伸长率 | 50 % | ISO 527-1/-2 | Cond. |
标称断裂伸长率 | 50 % | ISO 527-1/-2 | Dry |
拉伸模量 | 2020 Mpa | ISO 527-1/-2 | Cond. |
拉伸模量 | 2100 Mpa | ISO 527-1/-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 13 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | 13 kJ/m² | ISO 179/1eA | Cond. |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Cond. |
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Cond. |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 79 D | ISO 7619-1 | 15s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 150 °C | ISO 75-1/-2 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 136 °C | ISO 75-1/-2 | Dry |
维卡软化温度(Vicat) | 160 °C | ISO 306 | Dry, 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 70 E-6/K | ISO 11359-1/-2 | Dry |
熔融温度(Tm) | 168 °C | ISO 11357-1/-3 | Dry, 10°C/min |
加工温度 | 270 °C | - | Injection Molding |
模具温度 | 60 °C | - | Injection Molding |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.8 mm | IEC 60695-11-10 | Dry |
V-2 | 1.6 mm | IEC 60695-11-10 | Dry |
氧指数(LOI) | 26 % | ISO 4589-1/-2 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+11 Ohm-m | IEC 60093 | Cond. |
表面电阻率 | 1.0E+12 Ohm | IEC 60093 | Cond. |
相比漏电起痕指数(CTI ) | |||
- | 600 - | IEC 60112 | Cond. |
绝缘强度 | 50 kV/mm | IEC 60243-1 | Cond. |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 91 % | ISO 13468 | Dry |