Zytel® RS LC2600 BK043A
Zytel® RS LC2600 BK043A
PA (尼龙-聚酰胺)
杜邦 (DuPont)
产品描述
Zytel® RS LC2600 BK043A is a renewably sourced long chain polyamide, containing more than 50% renewably sourced ingredient by weight. It is a flexible, plasticized, high viscosity, black extrusion grade developed for air brake tubes and fluid handling ap
基本信息
| 原厂资料 | 物性表-ISO(中文) |
| 产品特性 | 高粘度 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1050 kg/m³
| ISO 1183 | |
吸湿率 | 1 %
| ISO 62 | 2mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
36 Mpa | ISO 527-1/-2 | |
断裂(brk) |
45 Mpa | ISO 527-1/-2 | |
断裂(brk) |
44 Mpa | ISO 527-1/-2 | Conditioned |
拉伸延伸率 | | | |
屈服(yld) |
30 % | ISO 527-1/-2 | |
断裂(brk) |
300 % | ISO 527-1/-2 | |
断裂(brk) |
330 % | ISO 527-1/-2 | Conditioned |
标称断裂伸长率 |
50 % | ISO 527-1/-2 | |
弯曲强度 | | | |
- |
18 Mpa | ISO 178 | at 3.5%, Conditioned |
- |
35 Mpa | ISO 178 | at 3.5%, Dry |
弯曲模量 | 900 Mpa
| ISO 178 | |
弯曲模量 | 470 Mpa
| ISO 178 | Conditioned |
拉伸模量 | 1150 Mpa
| ISO 527-1/-2 | |
拉伸模量 | 660 Mpa
| ISO 527-1/-2 | Conditioned |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
11 kJ/m² | ISO 179/1eA | |
23℃ (73℉) |
65 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | | | |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
43 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 220 °C
| ISO 11357-1/-3 | 10℃/min |
玻璃化温度(Tg) | 40 °C
| ISO 11357-1/-2 | 10℃/min |
玻璃化温度(Tg) | 30 °C
| ISO 11357-1/-2 | 10℃/min, Conditioned |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
FMVSS | B -
| FMVSS 302 | |
燃烧速率 | 100 mm/min
| ISO 3795 | 1mm |