Rilsan® Clear G170 MED
PA (尼龙-聚酰胺)
阿科玛 (Arkema)
产品描述
Rilsan® Clear G170 MED is a high performance transparent polyamide resin with outstanding thermal resistance. This grade offers the highest quality and is specifically designed to meet the stringent requirements of the medical applications. Upon request letters regarding USP class VI compliance can be provided.
Main applications:
- Medical perfusion tube accessories.
- Breathing mask.
Packaging:
This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.
Shelf Life:
Two years from the delivery. For any use above this limit, please refer to our technical services.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐热医疗级 | |||
| 法规认证 | USP Class VI(美国药典) | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.05 g/cm³ | ISO 1183 | Cond. |
密度 | 1.05 g/cm³ | ISO 1183 | Dry |
熔体体积流动速率(MVR) | |||
275°C/2.16 kg | 2 cm³/10 min | ISO 1133 | Dry |
收缩率 | |||
纵向(Flow) | 0.7 % | ISO 294-4, 2577 | Dry |
横向(Across Flow) | 0.7 % | ISO 294-4, 2577 | Dry |
吸水率 | 3.8 % | ISO 62 | Dry |
吸湿率 | 1.7 % | ISO 62 | Dry |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 74 Mpa | ISO 527-1/-2 | Cond. |
屈服(yld) | 76 Mpa | ISO 527-1/-2 | Dry |
拉伸延伸率 | |||
屈服(yld) | 9 % | ISO 527-1/-2 | Cond. |
屈服(yld) | 8 % | ISO 527-1/-2 | Dry |
标称断裂伸长率 | 50 % | ISO 527-1/-2 | Cond. |
标称断裂伸长率 | 50 % | ISO 527-1/-2 | Dry |
拉伸模量 | 2020 Mpa | ISO 527-1/-2 | Cond. |
拉伸模量 | 2100 Mpa | ISO 527-1/-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 13 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | 13 kJ/m² | ISO 179/1eA | Cond. |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Cond. |
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Cond. |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 79 D | ISO 7619-1 | 15s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 150 °C | ISO 75-1/-2 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 136 °C | ISO 75-1/-2 | Dry |
维卡软化温度(Vicat) | 160 °C | ISO 306 | Dry, 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 70 E-6/K | ISO 11359-1/-2 | Dry |
熔融温度(Tm) | 168 °C | ISO 11357-1/-3 | Dry, 10°C/min |
加工温度 | 270 °C | - | Injection Molding |
模具温度 | 60 °C | - | Injection Molding |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.8 mm | IEC 60695-11-10 | Dry |
V-2 | 1.6 mm | IEC 60695-11-10 | Dry |
氧指数(LOI) | 26 % | ISO 4589-1/-2 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+11 Ohm-m | IEC 60093 | Cond. |
表面电阻率 | 1.0E+12 Ohm | IEC 60093 | Cond. |
相比漏电起痕指数(CTI ) | |||
- | 600 - | IEC 60112 | Cond. |
绝缘强度 | 50 kV/mm | IEC 60243-1 | Cond. |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 91 % | ISO 13468 | Dry |