ExxonMobil™ LLDPE LL 3001.63
LLDPE
埃克森美孚化工(ExxonMobil Chemical)
产品描述
ExxonMobil™ LL 3001.63 is an ethylene 1-hexene linear low density polyethylene resin formulated for blown film extrusion. Films made from this resin have outstanding tensile and toughness properties. Superior strength properties, along with excellent drawability, make this a very versatile packaging film resin.
基本信息
| 原厂资料 | 物性表(英文) 物性表(中文) | |||
| 添加助剂 | 热稳定剂加工助剂 | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 薄膜挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.917 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 124 °C | Internal | Peak |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 13 % | ASTM D1003 | |
光泽度 | 38 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 9.3 Mpa | ASTM D 882 | MD |
屈服(yld) | 9.9 Mpa | ASTM D 882 | TD |
断裂(brk) | 50 Mpa | ASTM D 882 | MD |
断裂(brk) | 47 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 540 % | ASTM D 882 | MD |
断裂(brk) | 790 % | ASTM D 882 | TD |
穿透强度 | 41 N | Internal | |
耐穿透性 | 3.4 J | Internal | |
埃尔曼多夫撕裂 | 310 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 710 g | ASTM D 1922 | TD |
割线模量 | 190 Mpa | ASTM D 882 | 1% Secant, MD |
割线模量 | 240 Mpa | ASTM D 882 | 1% Secant, TD |
落锤冲击 | 170 g | ASTM D 1709 |