产品描述
Borstar LE8706 is a natural colourable linear low density (LLD) jacketing compound, which is produced with the Borealis proprietary Borstar bimodal process technology. Borstar technology allows the manufacturing of polymers outside the traditional MFR and density range making it possible to optimize processability, reduce shrinkage and yet provide excellent physical toughness and environmental stress crack resistance (ESCR).
Borstar LE8706 contains a well dispersed UV-stabiliser in sufficient amount providing a measure of weathering resistance.
Applications
Borstar LE8706 is designed for jacketing of energy and communication cables.
The abrasion resistance combined with low coefficient of friction makes it ideally suitable for the jacketing of energy and communication cables.
Borstar LE8706 offers a balance of properties giving advantages in manufacturing, installation and lifetime performance of communication and energy cables.
Specifications
Borstar LE8706 meets the applicable requirements as below when processed using sound extrusion practice and testing procedure: ASTM D 1248 Type I, Class A, Category 4, Grade E4, E5, J3 ISO 1872-PE KHLN 23-D012
The following cable material standards are met by Borstar LE8706: EN 50290-2-24 DMP 5, 6, 13, 16, 18
Cables manufactured with Borstar LE8706 using sound extrusion practice normally comply with the following cable product standards: IEC 60840, Type ST7 IEC 60502, Part 2, Type ST7 HD 603 S1, DMP 6 HD 620 S2 Part 1, table 4B, DMP 5, 13, 16, 18
Special Features
Borstar LE8706 consists of specially selected components to offer: Superior processability Excellent environmental stress cracking resistance (ESCR) Heat deformation resistance Low coefficient of friction Low water permeability Good petroleum-jelly resistance Very good UV resistance Low shrinkage
基本信息
原厂资料 | 物性表-ISO(英文) | |||
产品特性 | 低摩擦低收缩易成型抗紫外线ESCR | |||
添加助剂 | 紫外线稳定剂 | |||
颜色形状 | 本色 | |||
成型方式 | 线缆挤出 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 0.923 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.85 g/10min | ISO 1133 | |
环境应力开裂(ESCR ) | 5000 Hours | IEC 60811-406 | 50 °C, Igepal 10 %, F0 |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 28 Mpa | ISO 527-2 | 50 mm/min |
拉伸延伸率 | |||
断裂(brk) | 800 % | ISO 527-2 | 50 mm/min |
弯曲模量 | 400 Mpa | ISO 178 | |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
脆化温度 | -76 °C | ASTM D 746 | |
硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 52 D | ISO 868 | 1 s |
电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | IEC 60093 | |
介电常数(DK) | |||
1MHz | 2.3 - | IEC 60250 | |
耗散因数(DF) | |||
1MHz | 1.5 E-4 | IEC 60250 | |
绝缘强度 | 20 kV/mm | IEC 60243 |