Lotrène® LLDPE Q1018N
LLDPE
卡塔尔石化/梦塔佳(Muntajat)
产品描述
Lotrène Q1018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer.
They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties. Lotrène Q1018 Series are suited for many applications in the field of consumer, agricultural, industrial, food or hygiene packaging, for example: collation shrink, liners, FFS bags, heavy duty sacks, refuse, tunnel films, mulching films...
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 食品接触级 | |||
| 成型方式 | 薄膜挤出吹膜共挤共混改性 | |||
| 应用产品 | 重型塑料袋薄膜塑料袋共混食品包装包装 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.918 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 100 °C | ASTM D1525 | A120 |
结晶温度 | 122 °C | Internal | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 11 % | ASTM D1003 | 40 µm, Blown Film |
光泽度 | 60 - | ASTM D 2457 | 45°, 40 µm, Blown Film |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
薄膜测试厚度 | 40 μm | Internal | Blown Film |
拉伸强度 | |||
屈服(yld) | 11 Mpa | ASTM D 882 | MD |
屈服(yld) | 11 Mpa | ASTM D 882 | TD |
断裂(brk) | 33 Mpa | ASTM D 882 | MD |
断裂(brk) | 38 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 850 % | ASTM D 882 | MD |
断裂(brk) | 800 % | ASTM D 882 | TD |
埃尔曼多夫撕裂 | 120 N/mm | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 480 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 70 N/mm | ASTM D 1922 | TD |
埃尔曼多夫撕裂 | 280 g | ASTM D 1922 | TD |
割线模量 | 245 Mpa | ASTM D 882 | MD,1% Secant |
割线模量 | 215 Mpa | ASTM D 882 | TD, 1% Secant |
落锤冲击 | 150 g | ASTM D 1709 | F50 |