LLDPE TUFLIN™ HS-7066 NT 7

TUFLIN™ HS-7066 NT 7

TUFLIN™ HS-7066 NT 7

LLDPE

陶氏化学(Dow Chemical)

产品描述

TUFLIN™ HS-7066 NT 7 Linear Low Density Polyethylene Resin is a fractional melt, ethylene-hexene copolymer, linear low density (LLDPE) resin designed for good toughness and stiffness. This product is recommended for thin and thick gauge applications such as consumer trash bags and industrial heavy-duty shipping sacks that require strength and machinability.

  • Hexene Linear Low Density Resin

  • Good Strength and Stiffness

  • Complies with U.S. FDA 21 177.1520 (c) 3.2a

  • Consult the regulations for complete details.

    基本信息
    原厂资料
    物性表(英文)
    法规认证
    FDA(食品药品监督管理局)
    成型方式
    吹膜
    技术参数
    物理性能 值/单位 测试标准 测试条件

    密度

    0.926 g/cm³ ASTM D792

    密度

    0.926 g/cm³ Internal
    Base Density

    熔体质量流动速率(MFR)

    190℃/2.16 kg

    0.8 g/10min ASTM D1238
    热学性能 值/单位 测试标准 测试条件

    维卡软化温度(Vicat)

    113 °C ASTM D1525

    熔融温度(Tm)

    125 °C Internal
    DSC

    加工温度

    234 °C -
    Melt Temperature
    光学性能 值/单位 测试标准 测试条件

    雾度

    9 % ASTM D1003
    20.3 µm

    雾度

    16 % ASTM D1003
    50.8 µm

    光泽度

    56 - ASTM D 2457
    20.3 µm

    光泽度

    66 - ASTM D 2457
    20.3 µm

    光泽度

    54 - ASTM D 2457
    50.8 µm

    光泽度

    55 - ASTM D 2457
    50.8 µm
    薄膜性能 值/单位 测试标准 测试条件

    拉伸强度

    屈服(yld)

    16.3 Mpa ASTM D 882
    MD, 20 µm

    屈服(yld)

    14.8 Mpa ASTM D 882
    MD, 51 µm

    屈服(yld)

    19.7 Mpa ASTM D 882
    TD, 20 µm

    屈服(yld)

    16 Mpa ASTM D 882
    TD, 51 µm

    断裂(brk)

    58.8 Mpa ASTM D 882
    MD, 20 µm

    断裂(brk)

    52.9 Mpa ASTM D 882
    MD, 51 µm

    断裂(brk)

    43.1 Mpa ASTM D 882
    TD, 20 µm

    断裂(brk)

    46 Mpa ASTM D 882
    TD, 51 µm

    拉伸延伸率

    断裂(brk)

    600 % ASTM D 882
    MD, 20 µm

    断裂(brk)

    790 % ASTM D 882
    MD, 51 µm

    断裂(brk)

    730 % ASTM D 882
    TD, 20 µm

    断裂(brk)

    850 % ASTM D 882
    TD, 51 µm

    穿透强度

    40 N Internal
    20 µm

    穿透强度

    80.1 N Internal
    51 µm

    耐穿透性

    14.2 J/cm³ Internal
    20 µm

    耐穿透性

    2.37 J Internal
    20 µm

    耐穿透性

    13.2 J/cm³ Internal
    51 µm

    耐穿透性

    5.42 J Internal
    51 µm

    抗拉韧性

    300 J/cm³ ASTM D882
    MD, 20 µm

    抗拉韧性

    348 J/cm³ ASTM D882
    MD, 51 µm

    抗拉韧性

    321 J/cm³ ASTM D882
    TD, 20 µm

    抗拉韧性

    353 J/cm³ ASTM D882
    TD, 51 µm

    埃尔曼多夫撕裂

    180 g ASTM D 1922
    MD, 20 µm

    埃尔曼多夫撕裂

    470 g ASTM D 1922
    MD, 51 µm

    埃尔曼多夫撕裂

    650 g ASTM D 1922
    TD, 20 µm

    埃尔曼多夫撕裂

    1100 g ASTM D 1922
    TD, 51 µm

    割线模量

    276 Mpa ASTM D 882
    2% Secant, MD, 20 µm

    割线模量

    282 Mpa ASTM D 882
    2% Secant, MD, 51 µm

    割线模量

    333 Mpa ASTM D 882
    2% Secant, TD, 20 µm

    割线模量

    333 Mpa ASTM D 882
    2% Secant, TD, 51 µm

    落锤冲击

    58 g ASTM D 1709
    20 µm, A

    落锤冲击

    100 g ASTM D 1709
    20 µm, B

    落锤冲击

    190 g ASTM D 1709
    51 µm, A

    落锤冲击

    100 g ASTM D 1709
    51 µm, B

    低密封初始温度(SIT)

    120 ℃ Internal
    20 µm

    低密封初始温度(SIT)

    130 ℃ Internal
    51 µm