DOWLEX™ 2070G
LLDPE
陶氏化学(Dow Chemical)
产品描述
Linear Low Density Polyethylene
High strength in food packaging applications
Good processability at narrow die gaps
Complies with:
U.S. FDA 21 CFR 177.1520 (c) 3.2a
Canadian HPFB No Objection (With Limitations)
EU, No 10/2011
Consult the regulations for complete details.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 添加助剂 | 增滑剂开口剂 | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局)HPFB (加拿大健康产品和食品局) | |||
| 成型方式 | 吹膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.922 g/cm³ | ASTM D792 | |
密度 | 0.921 g/cm³ | Internal | Base Density |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 104 °C | ASTM D1525 | |
熔融温度(Tm) | 123 °C | Internal | DSC |
加工温度 | 218 °C | - | Extrusion |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 11 % | ASTM D1003 | 20.3 µm |
雾度 | 12 % | ASTM D1003 | 50.8 µm |
光泽度 | 56 - | ASTM D 2457 | 45°, 20.3 µm |
光泽度 | 65 - | ASTM D 2457 | 45°, 50.8 µm |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 10.7 Mpa | ASTM D 882 | MD, 20 µm |
屈服(yld) | 10.5 Mpa | ASTM D 882 | MD, 51µm |
屈服(yld) | 11.4 Mpa | ASTM D 882 | TD, 20 µm |
屈服(yld) | 11.6 Mpa | ASTM D 882 | TD, 51 µm |
断裂(brk) | 38 Mpa | ASTM D 882 | MD, 20 µm |
断裂(brk) | 35.6 Mpa | ASTM D 882 | MD, 51µm |
断裂(brk) | 28 Mpa | ASTM D 882 | TD, 20 µm |
断裂(brk) | 29.1 Mpa | ASTM D 882 | TD, 51 µm |
拉伸延伸率 | |||
断裂(brk) | 440 % | ASTM D 882 | MD, 20 µm |
断裂(brk) | 620 % | ASTM D 882 | MD, 51µm |
断裂(brk) | 650 % | ASTM D 882 | TD, 20 µm |
断裂(brk) | 680 % | ASTM D 882 | TD, 51 µm |
耐穿透性 | 8.69 J/cm³ | Internal | 20 µm |
耐穿透性 | 5.79 J/cm³ | Internal | 51 µm |
抗拉韧性 | 76.4 J/cm³ | ASTM D882 | MD, 20 µm |
抗拉韧性 | 99 J/cm³ | ASTM D882 | MD, 51µm |
抗拉韧性 | 89.9 J/cm³ | ASTM D882 | TD, 20 µm |
抗拉韧性 | 97.1 J/cm³ | ASTM D882 | TD, 51 µm |
埃尔曼多夫撕裂 | 250 g | ASTM D 1922 | MD, 20 µm |
埃尔曼多夫撕裂 | 810 g | ASTM D 1922 | MD, 51µm |
埃尔曼多夫撕裂 | 690 g | ASTM D 1922 | TD, 20 µm |
埃尔曼多夫撕裂 | 1200 g | ASTM D 1922 | TD, 51 µm |
割线模量 | 183 Mpa | ASTM D 882 | 2% Secant, MD, 20 µm |
割线模量 | 192 Mpa | ASTM D 882 | 2% Secant, MD, 51 µm |
割线模量 | 211 Mpa | ASTM D 882 | 2% Secant, TD, 20 µm |
割线模量 | 228 Mpa | ASTM D 882 | 2% Secant, TD, 51 µm |
落锤冲击 | 150 g | ASTM D 1709 | 20 µm |
落锤冲击 | 310 g | ASTM D 1709 | 51 µm |