DOWLEX™ GM 8051G
LLDPE
陶氏化学(Dow Chemical)
产品描述
DOWLEX™ GM 8051G Polyethylene Resin is designed for use in a wide variety of film applications, in special for FFS and lamination multilayered films combining excellent optical properties, mechanicals and an additive package designed to enhance COF stability.
Main Characteristics
High toughness, processability and optical properties
Fully formulated, enhanced COF stability
Complies with:
U.S. FDA FCN 741
Consult the regulations for complete details.
Additives:
Slip: Yes
Antiblock: Yes
基本信息
原厂资料 | 物性表(英文) | |||
添加助剂 | 增滑剂开口剂 | |||
法规认证 | FDA(食品药品监督管理局) |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 0.921 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 0.919 g/10min | ASTM D1238 | |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 108 °C | ASTM D1525 | |
熔融温度(Tm) | 121 °C | Internal | DSC |
光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 11.4 % | ASTM D1003 | 50 µm |
光泽度 | 63 - | ASTM D 2457 | 45°,50 µm |
薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 7.2 Mpa | ASTM D 882 | MD |
屈服(yld) | 7.4 Mpa | ASTM D 882 | TD |
断裂(brk) | 43.4 Mpa | ASTM D 882 | MD |
断裂(brk) | 39.3 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 830 % | ASTM D 882 | MD |
断裂(brk) | 850 % | ASTM D 882 | TD |
耐穿透性 | 28.6 J/cm³ | Internal | 50 µm |
埃尔曼多夫撕裂 | 740 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 890 g | ASTM D 1922 | TD |
割线模量 | 178 Mpa | ASTM D 882 | 2% Secant, MD |
割线模量 | 203 Mpa | ASTM D 882 | 2% Secant, TD |
落锤冲击 | 600 g | ASTM D 1709 |