TUFLIN™ HS-7094 NT 7

TUFLIN™ HS-7094 NT 7

LLDPE

陶氏化学(Dow Chemical)

产品描述

TUFLIN™ HS-7094 NT 7 Linear Low Density Polyethylene Resin is a fractional melt, ethylene-hexene copolymer, linear low density (LLDPE) resin designed for good toughness and stiffness. This product is recommended for thin and thick gauge applications such as trash bags and heavy-duty shipping sacks that require strength and output.

  • Hexene Linear Low Density Resin

  • Good Strength and Stiffness

  • Good Processability at Narrow Die Gaps

  • Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a

  • Consult the regulations for complete details.

    基本信息
    原厂资料
    物性表(英文)
    添加助剂
    加工助剂
    开口剂
    法规认证
    FDA(食品药品监督管理局)
    成型方式
    吹膜
    技术参数
    物理性能 值/单位 测试标准 测试条件

    密度

    0.93 g/cm³ ASTM D792

    密度

    0.926 g/cm³ Internal
    Base Density

    熔体质量流动速率(MFR)

    190℃/2.16 kg

    0.8 g/10min ASTM D1238
    热学性能 值/单位 测试标准 测试条件

    维卡软化温度(Vicat)

    114 °C ASTM D1525

    熔融温度(Tm)

    126 °C Internal
    DSC

    加工温度

    233 °C -
    Melt Temperature
    光学性能 值/单位 测试标准 测试条件

    雾度

    18 % ASTM D1003
    20.3 µm

    雾度

    21 % ASTM D1003
    50.8 µm

    光泽度

    23 - ASTM D 2457
    20.3 µm

    光泽度

    43 - ASTM D 2457
    20.3 µm

    光泽度

    26 - ASTM D 2457
    50.8 µm

    光泽度

    44 - ASTM D 2457
    50.8 µm
    薄膜性能 值/单位 测试标准 测试条件

    拉伸强度

    屈服(yld)

    16.1 Mpa ASTM D 882
    MD, 20 µm

    屈服(yld)

    15.2 Mpa ASTM D 882
    MD, 51 µm

    屈服(yld)

    16.5 Mpa ASTM D 882
    TD, 20 µm

    屈服(yld)

    16.4 Mpa ASTM D 882
    TD, 51 µm

    断裂(brk)

    59.7 Mpa ASTM D 882
    MD, 20 µm

    断裂(brk)

    53.4 Mpa ASTM D 882
    MD, 51 µm

    断裂(brk)

    44.6 Mpa ASTM D 882
    TD, 20 µm

    断裂(brk)

    47.5 Mpa ASTM D 882
    TD, 51 µm

    拉伸延伸率

    断裂(brk)

    570 % ASTM D 882
    MD, 20 µm

    断裂(brk)

    740 % ASTM D 882
    MD, 51 µm

    断裂(brk)

    840 % ASTM D 882
    TD, 20 µm

    断裂(brk)

    850 % ASTM D 882
    TD, 51 µm

    穿透强度

    31.1 N Internal
    20 µm

    穿透强度

    66.7 N Internal
    51 µm

    耐穿透性

    8.36 J/cm³ Internal
    20 µm

    耐穿透性

    1.47 J Internal
    20 µm

    耐穿透性

    7.03 J/cm³ Internal
    51 µm

    耐穿透性

    3.16 J Internal
    51 µm

    抗拉韧性

    300 J/cm³ ASTM D882
    MD, 20 µm

    抗拉韧性

    337 J/cm³ ASTM D882
    MD, 51 µm

    抗拉韧性

    344 J/cm³ ASTM D882
    TD, 20 µm

    抗拉韧性

    357 J/cm³ ASTM D882
    TD, 51 µm

    埃尔曼多夫撕裂

    170 g ASTM D 1922
    MD, 20 µm

    埃尔曼多夫撕裂

    590 g ASTM D 1922
    MD, 51 µm

    埃尔曼多夫撕裂

    800 g ASTM D 1922
    TD, 20 µm

    埃尔曼多夫撕裂

    1300 g ASTM D 1922
    TD, 51 µm

    割线模量

    302 Mpa ASTM D 882
    2% Secant, MD, 20 µm

    割线模量

    290 Mpa ASTM D 882
    2% Secant, MD, 51 µm

    割线模量

    327 Mpa ASTM D 882
    2% Secant, TD, 20 µm

    割线模量

    322 Mpa ASTM D 882
    2% Secant, TD, 51 µm

    落锤冲击

    52 g ASTM D 1709
    20 µm, A

    落锤冲击

    100 g ASTM D 1709
    20 µm, B

    落锤冲击

    170 g ASTM D 1709
    51 µm, A

    落锤冲击

    100 g ASTM D 1709
    51 µm, B

    低密封初始温度(SIT)

    120 ℃ Internal
    20 µm

    低密封初始温度(SIT)

    130 ℃ Internal