ExxonMobil™ LLDPE LL 1002BU
LLDPE
埃克森美孚化工(ExxonMobil Chemical)
产品描述
ExxonMobil™ LL 1002BU resin is an ethylene 1-butene linear low density polyethylene designed for the blown film process. It offers high gloss and excellent draw down. Films made from LL 1002BU have very good tensile and toughness properties. TnPP is not intentionally added to LL 1002BU resin.
基本信息
| 原厂资料 | 物性表(英文) 物性表(中文) | |||
| 添加助剂 | 热稳定剂增滑剂开口剂 | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 流延薄膜成型灌装封口(FFS)薄膜挤出吹膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.918 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 94 °C | Internal | |
熔融温度(Tm) | 123 °C | Internal | Peak |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 23 % | ASTM D1003 | |
光泽度 | 28 - | ASTM D 2457 | 45° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 8.7 Mpa | ASTM D 882 | MD |
屈服(yld) | 9.8 Mpa | ASTM D 882 | TD |
断裂(brk) | 36 Mpa | ASTM D 882 | MD |
断裂(brk) | 27 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 620 % | ASTM D 882 | MD |
断裂(brk) | 770 % | ASTM D 882 | TD |
穿透强度 | 21 N | Internal | |
耐穿透性 | 0.8 J | Internal | |
埃尔曼多夫撕裂 | 110 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 390 g | ASTM D 1922 | TD |
割线模量 | 170 Mpa | ASTM D 882 | 1% Secant, MD |
割线模量 | 210 Mpa | ASTM D 882 | 1% Secant, TD |
落锤冲击 | 60 g | ASTM D 1709 |