SABIC® LLDPE 318BJ
LLDPE
沙特基础 (SABIC)
产品描述
SABIC® LLDPE 318BJ is a butene linear low density polyethylene resin typically designed for easy processing and specially formulated for optimum thermal stability at high temperatures used in cast film extrusion. Cast film produced from SABIC® LLDPE 318BJ exhibit excellent optical properties, puncture resistance and tear strength .SABIC® LLDPE 318BJ is TNPP free. This product is not intended for and must not be used in any pharmaceutical/medical applications.
TYPICAL APPLICATIONS
SABIC® LLDPE 318BJ resin is typcially used for hand and pallet stretch wrap, cling film, melt embossed film and other genera-purpose application.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 成型方式 | 流延薄膜薄膜挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.918 g/cm³ | ASTM D 1505 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2.8 g/10min | ASTM D1238 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 98 °C | ASTM D1525 | |
加工温度 | 250~300 °C | - | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 5 % | ASTM D1003 | 30 μm film |
光泽度 | 90 - | ASTM D 2457 | at 60° |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 13 Mpa | ASTM D 882 | MD |
屈服(yld) | 10 Mpa | ASTM D 882 | TD |
断裂(brk) | 28 Mpa | ASTM D 882 | MD |
断裂(brk) | 18 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 470 % | ASTM D 882 | MD |
断裂(brk) | 600 % | ASTM D 882 | TD |
穿透强度 | 5700 J/m | Internal | |
埃尔曼多夫撕裂 | 65 g | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 300 g | ASTM D 1922 | TD |
割线模量 | 135 Mpa | ASTM D 882 | MD, 1% secant |
割线模量 | 140 Mpa | ASTM D 882 | TD, 1% secant |
落锤冲击 | 75 g | ASTM D 1709 |