DOWLEX™ 4056.01G
LLDPE
陶氏化学(Dow Chemical)
产品描述
DOWLEX™ 4056.01G is a linear low density resin designed for high quality blown film applications requiring a combination of excellent optical properties, tear strength, sealability and excellent processability. DOWLEX 4056.01G is also designed to offer a low gel level making it ideal for use in lamination films and other specialty packaging applications. This resin contains slip and antiblock additives.
Complies with:
EU, No 10/2011
U.S. FDA FCN 741
Consult the regulations for complete details.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 添加助剂 | 增滑剂开口剂 | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局) | |||
| 成型方式 | 吹膜 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.919 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 1.3 g/10min | ASTM D1238 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
摩擦系数 | 0.15 - | ASTM 1894 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
加工温度 | 217 °C | - | Extrusion |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 6.3 % | ASTM D1003 | 25 µm |
雾度 | 4.2 % | ASTM D1003 | 25 µm, With 20% LDPE |
雾度 | 4.2 % | ASTM D1003 | 25 µm, With 40% LDPE |
雾度 | 9.6 % | ASTM D1003 | 50 µm |
雾度 | 5.1 % | ASTM D1003 | 50 µm, With 20% LDPE |
雾度 | 5.1 % | ASTM D1003 | 50 µm, With 40% LDPE |
光泽度 | 65 - | ASTM D 2457 | 25 µm |
光泽度 | 81 - | ASTM D 2457 | 25 µm, With 20% LDPE |
光泽度 | 75 - | ASTM D 2457 | 25 µm, With 40% LDPE |
光泽度 | 64 - | ASTM D 2457 | 50 µm |
光泽度 | 80 - | ASTM D 2457 | 50 µm, With 20% LDPE |
光泽度 | 71 - | ASTM D 2457 | 50 µm, With 40% LDPE |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
穿透强度 | 8.6 N | Internal | 25 µm |
穿透强度 | 10.8 N | Internal | 50 µm |
耐穿透性 | 1.7 J | Internal | 25 µm |
耐穿透性 | 103 J/cm³ | Internal | 25 µm |
耐穿透性 | 4.3 J | Internal | 50 µm |
耐穿透性 | 124 J/cm³ | Internal | 50 µm |
埃尔曼多夫撕裂 | 280 g | ASTM D 1922 | MD, 25 µm |
埃尔曼多夫撕裂 | 650 g | ASTM D 1922 | MD, 50 µm |
埃尔曼多夫撕裂 | 420 g | ASTM D 1922 | TD, 25 µm |
埃尔曼多夫撕裂 | 750 g | ASTM D 1922 | TD, 50 µm |
落锤冲击 | 250 g | ASTM D 1709 | 25 µm |
落锤冲击 | 370 g | ASTM D 1709 | 50 µm |
低密封初始温度(SIT) | 105 ℃ | Internal | 25 µm |
低密封初始温度(SIT) | 105 ℃ | Internal | 50 µm |